Name: hydroquinone based synthesis of gold nanorods
Uploaded: 2016-08-10T14:00:00.000+00:00
Duration: 8 min 55 s
Description: Watch this Scientific Journal Video about Hydroquinone Based Synthesis of Gold Nanorods at JoVE.com

Funding for this research was provided by the Italian Ministry of Health under the frame of EuroNanoMed II (European Innovative Research &amp; Technological Development Projects in Nanomedicine, project title: ''InNaSERSS'').

1. Synthesis of Gold Nanorods
Note: Use highly purified water throughout.
<ol>
	<li>Preparation of the gold seeds
	<ol>
		<li>Dissolve 364.4 mg of hexadecyltrimethylammonium bromide (CTAB) in 5 ml water, under ultrasonication at 40 &#176;C until the solution becomes clear. Let the CTAB solution cool down to room temperature.</li>
		<li>Separately, prepare 5 ml of tetrachloroauric acid (HAuCl4) in water (0.5 mM).</li>
		<li>Add the HAuCl4 solution to the CTAB solution under vigorous magnetic stirring, maintaining the temperature constant at 27 &#176;C.</li>
		<li>Prepare 600 &#181;l of sodium borohydride (NaBH4) solution in water (10 mM) at 4 &#176;C. Add this solution to the mixture under vigorous stirring. Check if the solution&#39;s color immediately changes from yellow to brownish.</li>
		<li>Stir the suspension for 20 min before use. Store the seeds suspension for no longer than 24 hr at room temperature.</li>
		<li>Check the dimensions of the seeds using an UV-Vis spectrophotometer. Ensure that the seeds are small enough (about 2 nm) to be used in the preparation of gold nanorods by UV-visible spectroscopy. 
		Note: Spectrum must be similar to what is reported in Figure 1. Larger seeds identified by the presence of a plasmonic peak around 505-520 nm must not be used because they are likely to produce spherical nanoparticles.</li>
	</ol>
	</li>
	<li>Preparation of the &#34;growth solution&#34; of gold nanorods.
	<ol>
		<li>Dissolve 182.2 mg CTAB together with 22 mg hydroquinone in 5 ml water at 40 &#176;C using ultrasonication. Cool down the solution to 27 &#176;C.</li>
		<li>Prepare 200 &#181;l of 4 mM silver nitrate (AgNO3) solution.</li>
		<li>Separately, prepare 5 ml of 1 mM solution of tetrachloroauric acid (HAuCl4).</li>
		<li>First add the silver nitrate solution prepared in step 1.2.2. Then, add the HAuCl4 solution prepared in step 1.2.3 to the solution of CTAB and hydroquinone prepared in step 1.2.1 under magnetic stirring.</li>
		<li>Immediately after, add under magnetic stirring 12 &#181;l of the seeds suspension previously prepared according to the protocol reported at step 1.1 and let the reaction start. Check if the suspension changes color in about 30 min.</li>
		<li>Control the formation of the nanorods by checking the UV-visible spectrum of the suspension, as described in section 4, every 5 min. Proceed until the spectrum is stable. To allow the complete formation of the nanorods, leave the suspension under stirring for further 30 min (Figure 2).</li>
		<li>Divide the suspension in tubes (1 ml of suspension for each tube) and centrifuge at 10,000 x g for 10 min. Gold nanorods form a dark precipitate at the bottom of the tube.</li>
		<li>Resuspend the precipitate of each tube in 1 ml of water. Mix together the content of the tubes and store the suspension of gold nanorods at room temperature.</li>
		<li>Characterize the obtained nanorods by UV-visible spectroscopy and transmission electron microscopy as described in section 4 (Figure 3).</li>
	</ol>
	</li>
</ol>
2. Tuning the Aspect Ratio of Nanorods by Varying the Concentration of Ag+ Ions
<ol>
	<li>Prepare a silver nitrate solution with a concentration of 4 mM, dissolving 3.4 mg AgNO3 in 5 ml of water.</li>
	<li>Prepare in three different vials the solution with CTAB and hydroquinone as described in section 1.2.1 and add respectively 100 &#181;l, 150 &#181;l or 200 &#181;l of silver nitrate solution.</li>
	<li>Add the HAuCl4 solution prepared according to step 1.2.3 and proceed with the preparation of gold nanorods as described from point 1.2.5.</li>
	<li>Characterize the obtained nanorods by UV-visible spectroscopy and transmission electron microscopy. Vials with lower amounts of Ag+ will result in shorter nanorods (aspect ratio of 2 and 2.2 respectively) (Figure 4).</li>
</ol>
3. Tuning the Aspect Ratio of Nanorods by Varying the Concentration of CTAB
<ol>
	<li>Prepare different batches of gold nanorods with different concentrations of CTAB in the &#34;growth solution&#34;. Use concentrations from 10 mM to 100 mM to produce gold nanorods having different size and aspect ratio. The concentrations of CTAB used in each experiment are summarized in Table 1 with the corresponding amount of milligrams used. Dissolve the different amounts of CTAB always with 22 mg of hydroquinone in 5 ml of water.</li>
	<li>Add 200 &#181;l of silver nitrate solution (prepared according to step 1.2.2) and 5 ml of HAuCl4 solution (prepared according how described in step 1.2.3) in each vial under magnetic stirring.</li>
	<li>Add 12 &#181;l of seeds suspension and observe the change in color of the final mixture.</li>
	<li>Stop the stirring when the suspension&#39;s color and the UV-visible spectrum are stabilized; the reaction time depends on the CTAB concentration in the growth solution.</li>
	<li>Centrifuge at 10,000 x g for 10 min and resuspend in water.</li>
	<li>Characterize the obtained nanorods by UV-visible spectroscopy and transmission electron microscopy. A lower concentration of CTAB will result in shorter nanorods while a higher concentration will give longer but larger nanorods. On contrary the aspect ratio of the nanorods will be higher in the range around 40-50 mM and will decrease both at lower and higher concentrations (Figure 5 and Figure 6).</li>
</ol>
4. Characterization of Gold Nanorods
<ol>
	<li>UV-visible Spectroscopy
	<ol>
		<li>Dilute 100 &#181;l of nanorods solution with 400 &#181;l of water in a plastic micro-cuvette and acquire the UV-visible absorption spectrum (wavelength range between 400 and 840 nm) according to manufacturer&#39;s protocol.</li>
		<li>Collect UV-visible spectra (wavelength range between 400 and 840 nm) of the growth solution every 5 min in order to study the kinetics of the reaction.</li>
	</ol>
	</li>
	<li>Transmission Electron Microscopy (TEM)
	<ol>
		<li>Collect TEM images of each sample of nanorods, for the measurement of the size and of the aspect ratio of the obtained nanorods. Prepare the samples by placing a drop of suspension (4 &#181;l) onto an ultra-thin Formvar-coated 200-mesh copper grids and leave to dry in air at 4 &#176;C. Analyze the sample at TEM using an accelerating voltage of 200 kV according to manufacturer&#39;s protocol.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Zhou, W., Gao, X., Liu, D., Chen, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+Nanoparticles+for+In+Vitro+Diagnostics.">Gold Nanoparticles for In Vitro Diagnostics.</a> Chem Rev. 115 (19), 10575-10636 (2015).</li><li>Bao, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+nanoprisms+as+optoacoustic+signal+nanoamplifiers+for+in+vivo+bioimaging+of+gastrointestinal+cancers.">Gold nanoprisms as optoacoustic signal nanoamplifiers for in vivo bioimaging of gastrointestinal cancers.</a> Small. 9 (1), 68-74 (2013).</li><li>Han, G., Ghosh, P., Rotello, V. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionalized+gold+nanoparticles+for+drug+delivery.">Functionalized gold nanoparticles for drug delivery.</a> Nanomedicine. 2 (1), 113-123 (2007).</li><li>Choi, W. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tumor+regression+in+vivo+by+photothermal+therapy+based+on+gold-nanorod-loaded,+functional+nanocarriers.">Tumor regression in vivo by photothermal therapy based on gold-nanorod-loaded, functional nanocarriers.</a> ACS Nano. 5 (3), 1995-2003 (2011).</li><li>Langille, M. R., Personick, M. L., Zhang, J., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Defining+Rules+for+the+Shape+Evolution+of+Gold+Nanoparticles+.">Defining Rules for the Shape Evolution of Gold Nanoparticles .</a> J. Am. Chem. Soc. 134 (35), 14542-14554 (2012).</li><li>Lohse, S. E., Murphy, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Quest+for+Shape+Control:+A+History+of+Gold+Nanorod+Synthesis.">The Quest for Shape Control: A History of Gold Nanorod Synthesis.</a> Chem. Mater. 25 (8), 1250-1261 (2013).</li><li>Weissleder, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+clearer+vision+for+in+vivo+imaging.">A clearer vision for in vivo imaging.</a> Nat. Biotech. 19 (4), 316-317 (2001).</li><li>Sau, T. K., Murphy, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Seeded+High+Yield+Synthesis+of+Short+Au+Nanorods+in+Aqueous+Solution.">Seeded High Yield Synthesis of Short Au Nanorods in Aqueous Solution.</a> Langmuir. 20 (15), 6414-6420 (2004).</li><li>Ratto, F., Matteini, P., Rossi, F., Pini, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+and+shape+control+in+the+overgrowth+of+gold+nanorods.">Size and shape control in the overgrowth of gold nanorods.</a> J. Nanopart. Res. 12, 2029-2036 (2010).</li><li>Morasso, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Control+of+size+and+aspect+ratio+in+hydroquinone-based+synthesis+of+gold+nanorods.">Control of size and aspect ratio in hydroquinone-based synthesis of gold nanorods.</a> J. Nanopart. Res. 17, 330-337 (2015).</li><li>Vigderman, L., Zubarev, E. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-yield+synthesis+of+gold+nanorods+with+longitudinal+SPR+peak+greater+than+1200+nm+using+hydroquinone+as+a+reducing+agent.">High-yield synthesis of gold nanorods with longitudinal SPR peak greater than 1200 nm using hydroquinone as a reducing agent.</a> Chem. Mater. 25 (8), 1450-1457 (2013).</li><li>Walsh, M. J., Barrow, S. J., Tong, W., Funston, A. M., Etheridge, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Symmetry+breaking+and+silver+in+gold+nanorod+growth.">Symmetry breaking and silver in gold nanorod growth.</a> ACS Nano. 9 (1), 715-724 (2015).</li></ol>

The authors have nothing to disclose.

The protocol presented here applies hydroquinone, an aromatic molecule characterized by a weak reduction potential, to produce gold nanorods. There are two main advantages of the present protocol toward the most commonly employed synthetic route based on the use of ascorbic acid: the first is that hydroquinone is able to almost quantitatively reduce the gold ions allowing the production of higher amount of gold nanorods.11 The latter is given by the fact that it requires a lower amount of CTAB and a subsequent...

Gold nanoparticles (AuNPs) are one of the most widespread and promising nanostructures to be used in biomedical applications. Their use is essential in many point-of-care in vitro diagnostics products.1 They have been proposed as an effective tool for a number of other different applications: as a contrast agent in imaging studies,2 as a drug delivery system3 and as drugs for light-induced thermotherapy (or photothermal therapy).4 The great potential of AuNPs has driven, in the last twenty years, intense research on the development of new synthesis that is able to increase the control on the size and shape obtained.5 This is because different kinds of AuNPs are in fact more suitable than others for specific applications.
Among the different gold nanostructures, gold nanorods (AuNRs) have emerged as one of the most interesting systems. AuNRs are characterized by two plasmonic peaks associated with the oscillation of electrons along the longitudinal and the transverse axes, respectively.6 It is particularly important that the position of the most intense longitudinal peak can be tuned precisely between 620 and 800 nm, depending on the aspect ratio of the rods. This region matches the biological window,7 where the human tissues almost do not absorb light, allowing the development of a number of in vivo photonic applications involving AuNPs.
Despite a huge interest in this kind of nanostructures, the synthetic protocols for the preparation of AuNRs suffer from several limitations. In most of the cases, nanorods are prepared according to a two-step method developed by Sau and coworkers.8 In their protocol, nanorods are synthesized by reducing gold ions using ascorbic acid in presence of preformed gold seeds, silver ions and a large amount of hexadecyl trimethylammonium bromide (CTAB), a cationic linear surfactant.
The drawback of this protocol is that the reduction yield of gold ions is relatively low (about 20%) 9 and that a high amount of CTAB, an expensive reagent that accounts for more than half of the total cost for the reagents in the synthesis, is needed. The development of a new and more efficient synthetic route is thence considered to be an important need, allowing the spreading of biomedical approaches based on AuNRs.
In the first part of the present paper, we present an optimized protocol for the preparation of AuNR having an aspect ratio of about three. The synthesis is based on the use of hydroquinone as a mild reducing agent and it allows the preparation of AuNR with an almost quantitative reduction of gold ions, making use of a reduced amount of CTAB.10 This protocol for the preparation of the AuNRs is based on a two-step approach where gold seeds are used in a &#34;growth solution&#34;.
In the second part, we show how to finely tune the size and aspect ratio of the obtained AuNR in two ways. The first way, similar to the standard protocol based on ascorbic acid, is to vary the amount of silver ions present in the &#34;growth solution&#34;. The second way is based on the variation of the amount of CTAB that can be reduced down to a concentration of 10 mM (close to the critical micellar concentration reported by the supplier) to obtain well defined short nanorods.

<table><tbody><tr><td>Gold(III) chloride trihydrate</td><td>Sigma Aldrich</td><td>520918</td><td></td></tr><tr><td>Hydroquinone</td><td>Sigma Aldrich</td><td>H17902</td><td></td></tr><tr><td>Silver Nitrate</td><td>Sigma Aldrich</td><td>209139</td><td>toxic</td></tr><tr><td>Sodium Borohydride</td><td>Sigma Aldrich</td><td>480886</td><td></td></tr><tr><td>Hexadecyltrimethylammonium bromide (CTAB)</td><td>Sigma Aldrich</td><td>H5882</td><td>Acute Tox. (oral). In this study we tested three different batches of CTAB (H5882) from Sigma Aldrich. Two of them were marked as made in China while one as made in India. In our experience only the batches marked as made in China were effective for the preparation of AuNR.</td></tr><tr><td>Spectrophotometer</td><td>Thermo scientific&amp;nbsp;</td><td>Nanodrop 2000C</td><td></td></tr><tr><td>TEM</td><td>JEOL</td><td>2100</td><td></td></tr></tbody></table>

hydroquinone based synthesis of gold nanorods

Gold nanorods are an important kind of nanoparticles characterized by peculiar plasmonic properties. Despite their widespread use in nanotechnology, the synthetic methods for the preparation of gold nanorods are still not fully optimized. In this paper we describe a new, highly efficient, two-step protocol based on the use of hydroquinone as a mild reducing agent. Our approach allows the preparation of nanorods with a good control of size and aspect ratio (AR) simply by varying the amount of hexadecyl trimethylammonium bromide (CTAB) and silver ions (Ag+) present in the "growth solution". By using this method, it is possible to markedly reduce the amount of CTAB, an expensive and cytotoxic reagent, necessary to obtain the elongated shape. Gold nanorods with an aspect ratio of about 3 can be obtained in the presence of just 50 mM of CTAB (versus 100 mM used in the standard protocol based on the use of ascorbic acid), while shorter gold nanorods are obtained using a concentration as low as 10 mM.

UV visible spectra of the gold seeds can be seen in Figure 1. UV visible spectra acquired at different times after the injection of the gold seeds are presented in Figure 2. UV visible spectra and transmission electron microscopic (TEM) images of the obtained gold nanorods are shown in Figure 3. UV visible spectra and transmission electron microscopic (TEM) images of gold nanorods with different aspect ratio obtained by varying the amount...

Watch this Scientific Journal Video about Hydroquinone Based Synthesis of Gold Nanorods at JoVE.com

Hydroquinone Based Synthesis of Gold Nanorods

This paper describes a protocol for the synthesis of gold nanorods, based on the use of hydroquinone as reducing agent, plus the different mechanisms for controlling their size and aspect ratio.

Gold nanorods are an important kind of nanoparticles characterized by peculiar plasmonic properties. Despite their widespread use in nanotechnology, the ...

hydroquinone-based-synthesis-of-gold-nanorods

Universidad San Sebastian

Research

JoVE Journal

Chemistry

13.6K Views.  Fondazione Don Carlo Gnocchi ONLUS (Don Carlo Gnocchi Foundation). This paper describes a protocol for the synthesis of gold nanorods, based on the use of hydroquinone as reducing agent, plus the different mechanisms for controlling their size and aspect ratio.

Video: Hydroquinone Based Synthesis of Gold Nanorods

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) membranes have been under development since the 1990's and have become a common method to template the synthesis of high aspect ratio nanostructures, mostly by electrochemical growth or pore-wetting. Recently, these membranes have become commercially available in a wide range of pore sizes and densities, leading to an extensive library of functional nanostructures being synthesized from AAO membranes. These include composite nanorods, nanowires and nanotubes made of metals, inorganic materials or polymers 3-10. Nanoporous membranes have been used to synthesize nanoparticle and nanotube arrays that perform well as refractive index sensors, plasmonic biosensors, or surface enhanced Raman spectroscopy (SERS) substrates 11-16, as well as a wide range of other fields such as photo-thermal heating 17, permselective transport 18, 19, catalysis 20, microfluidics 21, and electrochemical sensing 22, 23. Here, we report a novel procedure to prepare gold nanotubes in AAO membranes. Hollow nanostructures have potential application in plasmonic and SERS sensing, and we anticipate these gold nanotubes will allow for high sensitivity and strong plasmon signals, arising from decreased material dampening 15.

Solution-suspendable gold nanotubes with controlled dimensions can be synthesized by electrochemical deposition in porous anodic aluminum oxide (AAO) membranes using a hydrophobic polymer core. Gold nanotubes and nanotube arrays hold promise for applications in plasmonic biosensing, surface-enhanced Raman spectroscopy, photo-thermal heating, ionic and molecular transport, microfluidics, catalysis and electrochemical sensing.

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) ...

Gold Nanostar Synthesis with a Silver Seed Mediated Growth Method

The physical, chemical and optical properties of nano-scale colloids depend on their material composition, size and shape 1-5. There is a great interest in using nano-colloids for photo-thermal ablation, drug delivery and many other biomedical applications 6. Gold is particularly used because of its low toxicity 7-9. A property of metal nano-colloids is that they can have a strong surface plasmon resonance 10. The peak of the surface plasmon resonance mode depends on the structure and composition of the metal nano-colloids. Since the surface plasmon resonance mode is stimulated with light there is a need to have the peak absorbance in the near infrared where biological tissue transmissivity is maximal 11, 12.
We present a method to synthesize star shaped colloidal gold, also known as star shaped nanoparticles 13-15 or nanostars 16. This method is based on a solution containing silver seeds that are used as the nucleating agent for anisotropic growth of gold colloids 17-22. Scanning electron microscopy (SEM) analysis of the resulting gold colloid showed that 70 % of the nanostructures were nanostars. The other 30 % of the particles were amorphous clusters of decahedra and rhomboids. The absorbance peak of the nanostars was detected to be in the near infrared (840 nm). Thus, our method produces gold nanostars suitable for biomedical applications, particularly for photo-thermal ablation.

We synthesized star shaped gold nanostars using a silver seed mediated growth method. The diameter of the nanostars ranges from 200 to 300 nm and the number of tips vary from 7 to 10. The nanoparticles have a broad surface plasmon resonance mode centered in the near infrared.

The physical, chemical and optical properties of nano-scale colloids depend on their material composition, size and shape 1-5. There is a great interest ...

Bioengineering

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large extinction coefficients which can be tuned across the visible spectrum. Research into the plasmonic enhancement of optical transitions has become popular, due to the possibility of altering and in some cases improving photo-absorption or emission properties of nearby chromophores such as molecular dyes or quantum dots. The electric field of the plasmon can couple with the excitation dipole of a chromophore, perturbing the electronic states involved in the transition and leading to increased absorption and emission rates. These enhancements can also be negated at close distances by energy transfer mechanism, making the spatial arrangement of the two species critical. Ultimately, enhancement of light harvesting efficiency in plasmonic solar cells could lead to thinner and, therefore, lower cost devices. The development of hybrid core/shell particles could offer a solution to this issue. The addition of a dielectric spacer between a gold nanoparticles and a chromophore is the proposed method to control the exciton plasmon coupling strength and thereby balance losses with the plasmonic gains. A detailed procedure for the coating of gold nanoparticles with CdS and ZnS semiconductor shells is presented. The nanoparticles show high uniformity with size control in both the core gold particles and shell species allowing for a more accurate investigation into the plasmonic enhancement of external chromophores.

The synthesis of uniform gold nanoparticles coated with semiconductor shells of CdS or ZnS is performed. The semiconductor coating is conducted by first depositing a silver sulfide shell and exchanging the silver cations for zinc or cadmium cations.

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large ...

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions

Reducing dilute aqueous HAuCl4 with sodium thiocyanate (NaSCN) under alkaline conditions produces 2 to 3 nm diameter nanoparticles. Stable grape-like oligomeric clusters of these yellow nanoparticles of narrow size distribution are synthesized under ambient conditions via two methods. The delay-time method controls the number of subunits in the oligoclusters by varying the time between the addition of HAuCl4 to alkaline solution and the subsequent addition of reducing agent, NaSCN. The yellow oligoclusters produced range in size from ~3 to ~25 nm. This size range can be further extended by an add-on method utilizing hydroxylated gold chloride (Na+[Au(OH4-x)Clx]-) to auto-catalytically increase the number of subunits in the as-synthesized oligocluster nanoparticles, providing a total range of 3 nm to 70 nm. The crude oligocluster preparations display narrow size distributions and do not require further fractionation for most purposes. The oligoclusters formed can be concentrated &#62;300 fold without aggregation and the crude reaction mixtures remain stable for weeks without further processing. Because these oligomeric clusters can be concentrated before derivatization they allow expensive derivatizing agents to be used economically. In addition, we present two models by which predictions of particle size can be made with great accuracy.

We describe a simple method for producing highly stable oligomeric clusters of gold nanoparticles via the reduction of chloroauric acid (HAuCl4) with sodium thiocyanate (NaSCN). The oligoclusters have a narrow size distribution and can be produced with a wide range of sizes and surface coats.

Reducing dilute aqueous HAuCl4 with sodium thiocyanate (NaSCN) under alkaline conditions produces 2 to 3 nm diameter nanoparticles. Stable grape-like ...

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs within the interlayer space of semiconducting layered titania nanosheet (TNS) films was investigated here. Two types of intermediate films (i.e., TNS films containing methyl viologen (TNS/MV2+) and 2-ammoniumethanethiol (TNS/2-AET+)) were prepared. The two intermediate films were soaked in an aqueous tetrachloroauric(III) acid (HAuCl4) solution, whereby considerable amounts of Au(III) species were accommodated within the interlayer spaces of the TNS films. The two types of obtained films were then soaked in an aqueous sodium tetrahydroborate (NaBH4) solution, whereupon the color of the films immediately changed from colorless to purple, suggesting the formation of AuNPs within the TNS interlayer. When only TNS/MV2+ was used as the intermediate film, the color of the film gradually changed from metallic purple to dusty purple within 30 min, suggesting that aggregation of AuNPs had occurred. In contrast, this color change was suppressed by using the TNS/2-AET+ intermediate film, and the AuNPs were stabilized for over 4 months, as evidenced by the characteristic extinction (absorption and scattering) band from the AuNPs.

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Here, we present a protocol for the in situ synthesis of gold nanoparticles (AuNPs) within the interlayer space of layered titanate films without the aggregation of AuNPs. No spectral change was observed even after 4 months. The synthesized material has expected applications in catalysis, photo-catalysis, and the development of cost-effective plasmonic devices.

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs ...

Engineering

Synthesis and Characterization of Amphiphilic Gold Nanoparticles

Gold nanoparticles covered with a mixture of 1-octanethiol (OT) and 11-mercapto-1-undecane sulfonic acid (MUS) have been extensively studied because of their interactions with cell membranes, lipid bilayers, and viruses. The hydrophilic ligands make these particles colloidally stable in aqueous solutions and the combination with hydrophobic ligands creates an amphiphilic particle that can be loaded with hydrophobic drugs, fuse with the lipid membranes, and resist nonspecific protein adsorption. Many of these properties depend on nanoparticle size and the composition of the ligand shell. It is, therefore, crucial to have a reproducible synthetic method and reliable characterization techniques that allow the determination of nanoparticle properties and the ligand shell composition. Here, a one-phase chemical reduction, followed by a thorough purification to synthesize these nanoparticles with diameters below 5 nm, is presented. The ratio between the two ligands on the surface of the nanoparticle can be tuned through their stoichiometric ratio used during synthesis. We demonstrate how various routine techniques, such as transmission electron microscopy (TEM), nuclear magnetic resonance (NMR), thermogravimetric analysis (TGA), and ultraviolet-visible (UV-Vis) spectrometry, are combined to comprehensively characterize the physicochemical parameters of the nanoparticles.

Amphiphilic gold nanoparticles can be used in many biological applications. A protocol to synthesize gold nanoparticles coated by a binary mixture of ligands and a detailed characterization of these particles is presented.

Gold nanoparticles covered with a mixture of 1-octanethiol (OT) and 11-mercapto-1-undecane sulfonic acid (MUS) have been extensively studied because of ...

Assembly of Gold Nanorods into Chiral Plasmonic Metamolecules Using DNA Origami Templates

The inherent addressability of DNA origami structures makes them ideal templates for the arrangement of metal nanoparticles into complex plasmonic nanostructures. The high spatial precision of a DNA origami-templated assembly allows controlling the coupling between plasmonic resonances of individual particles and enables tailoring optical properties of the constructed nanostructures. Recently, chiral plasmonic systems attracted a lot of attention due to the strong correlation between the spatial configuration of plasmonic assemblies and their optical responses (e.g., circular dichroism [CD]). In this protocol, we describe the whole workflow for the generation of DNA origami-based chiral assemblies of gold nanorods (AuNRs). The protocol includes a detailed description of the design principles and experimental procedures for the fabrication of DNA origami templates, the synthesis of AuNRs, and the assembly of origami-AuNR structures. In addition, the characterization of structures using transmission electron microscopy (TEM) and CD spectroscopy is included. The described protocol is not limited to chiral configurations and can be adapted for the construction of various plasmonic architectures.

We describe the detailed protocol for the DNA origami-based assembly of gold nanorods into chiral plasmonic metamolecules with strong chiroptical responses. The protocol is not limited to chiral configurations and can be easily adapted for the fabrication of various plasmonic architectures.

The inherent addressability of DNA origami structures makes them ideal templates for the arrangement of metal nanoparticles into complex plasmonic ...

Preparation and Photoacoustic Analysis of Cellular Vehicles Containing Gold Nanorods

Gold nanorods are attractive for a range of biomedical applications, such as the photothermal ablation and the photoacoustic imaging of cancer, thanks to their intense optical absorbance in the near-infrared window, low cytotoxicity and potential to home into tumors. However, their delivery to tumors still remains an issue. An innovative approach consists of the exploitation of the tropism of tumor-associated macrophages that may be loaded with gold nanorods in vitro. Here, we describe the preparation and the photoacoustic inspection of cellular vehicles containing gold nanorods. PEGylated gold nanorods are modified with quaternary ammonium compounds, in order to achieve a cationic profile. On contact with murine macrophages in ordinary Petri dishes, these particles are found to undergo massive uptake into endocytic vesicles. Then these cells are embedded in biopolymeric hydrogels, which are used to verify that the stability of photoacoustic conversion of the particles is retained in their inclusion into cellular vehicles. We are confident that these results may provide new inspiration for the development of novel strategies to deliver plasmonic particles to tumors.

We show the preparation and address the feasibility of cellular vehicles containing gold nanorods for the photoacoustic imaging of cancer.

Gold nanorods are attractive for a range of biomedical applications, such as the photothermal ablation and the photoacoustic imaging of cancer, thanks to ...

Gold Nanoparticle Synthesis

Gold nanoparticles (Au nanoparticles) that are ~12 nm in diameter were synthesized by rapidly injecting a solution of 150 mg (0.15 mmol) of tetrachloroauric acid in 3.0 g (3.7 mmol, 3.6 mL) of oleylamine (technical grade) and 3.0 mL of toluene into a boiling solution of 5.1 g (6.4 mmol, 8.7 mL) of oleylamine in 147 mL of toluene. While boiling and mixing the reaction solution for 2 hours, the color of the reaction mixture changed from clear, to light yellow, to light pink, and then slowly to dark red. The heat was then turned off, and the solution was allowed to gradually cool down to room temperature for 1 hour. The gold nanoparticles were then collected and separated from the solution using a centrifuge and washed three times; by vortexing and dispersing the gold nanoparticles in 10 mL portions of toluene, and then precipitating the gold nanoparticles by adding 40 mL portions of methanol and spinning them in a centrifuge. The solution was then decanted to remove any remaining byproducts and unreacted starting materials. Drying the gold nanoparticles in a vacuum environment produced a solid black pellet; which could be stored for long periods of time (up to one year) for later use, and then redissolved in organic solvents such as toluene.

A protocol for synthesizing ~12 nm diameter gold nanoparticles (Au nanoparticles) in an organic solvent is presented. The gold nanoparticles are capped with oleylamine ligands to prevent agglomeration. The gold nanoparticles are soluble in organic solvents such as toluene.

Gold nanoparticles (Au nanoparticles) that are ~12 nm in diameter were synthesized by rapidly injecting a solution of 150 mg (0.15 mmol) of ...

Synthesis of Functionalized 10-nm Polymer-coated Gold Particles for Endothelium Targeting and Drug Delivery

Gold nanoparticles (AuNPs) have been used extensively in medical research due to their size, biocompatibility, and modifiable surface. Specific targeting and drug delivery are some of the applications of these AuNPs, but endothelial extracellular matrices&#39; defensive properties hamper particle uptake. To address this issue, we describe a synthesis method for ultrasmall gold nanoparticles to improve vascular delivery, with customizable functional groups and polymer lengths for further adjustments. The protocol yields 2.5 nm AuNPs that are capped with tetrakis(hydroxymethyl)phosphonium chloride (THPC). The replacement of THPC with hetero-functional polyethylene glycol (PEG) on the surface of the AuNP increases the hydrodynamic radius to 10.5 nm while providing various functional groups on the surface. The last part of the protocol includes an optional addition of a fluorophore to allow the AuNPs to be visualized under fluorescence to track nanoparticle uptake. Dialysis and lyophilization were used to purify and isolate the AuNPs. These fluorescent nanoparticles can be visualized in both in vitro and in vivo experiments due to the biocompatible PEG coating and fluorescent probes. Additionally, the size range of these nanoparticles render them an ideal candidate for probing the glycocalyx without disrupting normal vasculature function, which may lead to improved delivery and therapeutics.

We describe a method of synthesizing biocompatible 10-nm gold nanoparticles, functionalized by coating poly-ethylene glycol onto the surface. These particles can be used in vitro and in vivo for delivering therapeutics to nanoscale cellular and extracellular spaces that are difficult to access with conventional nanoparticle sizes.

Gold nanoparticles (AuNPs) have been used extensively in medical research due to their size, biocompatibility, and modifiable surface. Specific targeting ...

Hydroquinone Based Synthesis of Gold Nanorods

Podsumowanie

Przeglądaj więcej filmów

Rozdziały w tym wideo

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

Gold Nanostar Synthesis with a Silver Seed Mediated Growth Method

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Synthesis and Characterization of Amphiphilic Gold Nanoparticles

Assembly of Gold Nanorods into Chiral Plasmonic Metamolecules Using DNA Origami Templates

Preparation and Photoacoustic Analysis of Cellular Vehicles Containing Gold Nanorods

Gold Nanoparticle Synthesis

Synthesis of Functionalized 10-nm Polymer-coated Gold Particles for Endothelium Targeting and Drug Delivery