1. Thermoplastic Suspension for CerAM -&#160;T3DP
<ol>
	<li>Selection of powders
	<ol>
		<li>For the preparation of the black thermoplastic suspensions use black zirconia powders zirconia black - 1 and zirconia black - 2.</li>
		<li>For the preparation of the white thermoplastic suspensions use zirconia white - 1 and zirconia white - 2. 
		NOTE: The manufacturer of zirconia black - 2 uses pigments (4.2 wt.-%) for the coloring of the zirconia and also states that both powders have the same sintering behavior. Additionally, the high percentage of alumina (20.43 wt.-%) contributes to the white color of zirconia white - 2. The powders zirconia black - 1 and zirconia white - 1 have a different composition and thus require a different sintering temperature for complete densification. In contrast to zirconia white - 1, zirconia black - 1 consists at most 5 wt.-% pigments. The recommended sintering temperatures are 1400 &#176;C for zirconia black - 1 and 1350 &#176;C for zirconia white - 1.</li>
	</ol>
	</li>
	<li>Characterize the powders regarding&#160;shape, surface area and particle size distribution. 
	NOTE: Electron scanning microscopy images have been used to characterize the shape of the particles. The particle size distribution of the utilized powders was measured by a laser diffraction method (laser diffractometer). The measurements for the specific surface properties of the used powders have been provided by the manufacture.</li>
	<li>For the preparation of the different zirconia suspensions&#160;melt a mixture of paraffin and beeswax at a temperature of 100 &#176;C in a heatable dissolver and homogenize the polymer mixture.
	<ol>
		<li>Then add the powder in several steps to reach a powder content of 40&#160;vol.%.</li>
		<li>Homogenize the powder-polymer-mixture by stirring for 2 h at 100 &#176;C. Ensure that all suspensions have the same powder content (40&#160;vol.%).</li>
	</ol>
	</li>
	<li>Characterization of suspensions
	<ol>
		<li>Characterize the rheological behavior of the molten suspension using a rheometer for shear rates in a range between 0-5,000/s for different temperatures in a range between 85 &#176;C and 110 &#176;C. 
		NOTE: We used a rheometer&#160;adjustable between -25 &#176;C to 200 &#176;C with a plate/plate measuring system (25 mm diameter). The torque was measured, and the dynamic viscosity was calculated.</li>
		<li>Plot the dynamic viscosity as&#160;function of the shear rate and make sure that the dynamic viscosity is below 100 Pa&#183;s for a shear rate of 10/s, below 20 Pa&#183;s for a shear rate of 100/s and below 1 Pa&#183;s for a shear rate of 5,000/s or increase the temperature within the permissible range.</li>
		<li>Change the suspension composition by adding polymer mixture if the dynamic viscosity is too high even for a temperature of 110 &#176;C.</li>
	</ol>
	</li>
</ol>
2. Manufacturing of Single and Multi-Material Components by CerAM -&#160;T3DP
<ol>
	<li>Used device 
	Figure 1 shows a CAD-drawing of the used CerAM -&#160;T3DP-device with one profile scanner and three different micro dispensing systems, which can work simultaneously or alternately. Use two of them to produce black-and-white components.
	<ol>
		<li>Set the deposition of the droplets to a frequency up to 100/s and the axes to move with a maximum velocity of 20 mm/s.</li>
	</ol>
	</li>
	<li>Investigation of deposition parameters 
	Investigate the influence of deposition parameters (working velocities of the micro dispensing system; temperatures of suspension reservoir and nozzle; velocity of the axis) on the properties of the resulting droplets (shape; volume; homogeneity) or droplet chains (shape; volume; homogeneity).
	<ol>
		<li>Vary the deposition parameters and deposit single droplets as well as droplet chains by using different frequencies and axes velocities for deposition. 
		NOTE: The influence of the dispenser parameters on the properties of the materials has been discussed before25. Parameter value boundaries have only been determined&#160;empirically.</li>
		<li>Make sure that that the variance in droplet chain height and width should not exceed 3 %. Vary the parameters pulse width, droplet fusion factor (DFF) and extrusion width (slicing parameter) to compensate diameter differences up to 100 microns and height differences up to 50 microns. 
		NOTE: It is not necessary and probably not possible to realize perfectly shaped hemispheres as single droplets, but you have to make sure that the homogeneity of the droplet formation is very high to guarantee a homogenous building of the components.</li>
		<li>Repeat this step with different initial parameters to find a parameter set which provides the most homogenous droplet shape with respect to droplet diameter, width&#160;and height.</li>
	</ol>
	</li>
	<li>Manufacturing of single-material test components
	<ol>
		<li>Use a generated 3D model of the desired part and save the file as STL or AMF file format.</li>
		<li>Use a slicing program (e.g. Slicer 1 or Slicer 2) to generate the corresponding G-code. Set the properties for the droplet shape acquired in step 2.2.</li>
		<li>Upload the G-code and fill the process parameters to the CerAM -&#160;T3DP-device. Set the CerAM -&#160;T3DP-device for the parameters obtained in step 2.2 that did correspond to the droplet shape provided to the slicer. Start the device software to start the building job. 
		NOTE: It is beneficial to manufacture certain test samples before building the desired part or using new suspensions.</li>
	</ol>
	</li>
	<li>CerAM -&#160;T3DP of multi-material components
	<ol>
		<li>For each material involved execute step 2.2.</li>
		<li>Select dispensing parameters for both materials which have approximately the same droplet characteristics.</li>
		<li>Adjust the layer heights by changing the distance between the single droplets and the resulting overlap to avoid differences in heights for the different materials, which can result in large defects and faulty components. 
		NOTE: By reducing the distance between two droplets and the associated greater overlap, the width and height of the droplet chain increases due to the nearly constant volume of the single droplets. It can be observed that the droplet chain width increases faster than the droplet chain height.</li>
		<li>Use a generated 3D model of the desired part and save the file as AMF files. If supported by the slicer multiple component areas can also be saved in STL file format.</li>
		<li>In order to print multi-material components, assign corresponding component areas to the associated material in the slicing software by allocating a corresponding micro dispensing system for each material.</li>
		<li>Generate the G-codes for each material by using the slicer software.</li>
		<li>Upload the G-code and fill the process parameters to the CerAM -&#160;T3DP-device. Set the CerAM -&#160;T3DP-device for the parameters obtained in step 2.2 that did correspond to the droplet shape provided to the slicer. Start the device software to start the building job.</li>
	</ol>
	</li>
</ol>
3. Co-Debinding and Co-Sintering of Single- and Multi-Material Components
<ol>
	<li>Debind the green samples in the following separate steps.
	<ol>
		<li>First, put the samples in a loose bulk of coarse-grained alumina powder (powder bed) to structurally support the samples as well as to ensure a homogeneous temperature distribution and to promote the removal of the binder materials by capillary forces.</li>
		<li>Perform a debinding with a very low heating rate in a furnace (debinding furnace) under air-atmosphere up to 270 &#176;C. Set the heating rate to 4 K/h to ensure a defect-free debinding.</li>
	</ol>
	</li>
	<li>After this first debinding step carefully remove the bedding powder for example with a fine brush. Place the samples on alumina kiln furniture.</li>
	<li>Apply a second debinding step under air-atmosphere up to 900 &#176;C (12 K/h) in the same furnace. 
	NOTE: All remaining organic binder materials were thermally removed, while within in the same step a pre-sintering of the zirconia particles was initiated to enable the subsequent transfer of the samples to a sintering kiln.</li>
	<li>Finally&#160;sinter the samples under air-atmosphere at 1,350 &#176;C (180 K/h) for 2 h in a suitable furnace (sintering furnace). Characterize the shrinkage of the components by length measurement in three dimensions and make sure that it is about 20% for each direction.</li>
</ol>
4. Characterization of Single- and Multi-Material Components
<ol>
	<li>Cut the samples properly and polish the surface using ceramographic methods.</li>
	<li>Apply investigations on the microstructure by using Field Emission Scanning Electron Microscope (FESEM).</li>
	<li>Visually inspect the porosity of the two phases and at the boundary interface of the used materials. To obtain a more detailed result perform an interface analysis, e.g. by FESEM and subsequent picture analysis to investigate the porosity within the sintered microstructure. 
	The targeted porosity is below 1%. If the porosity is too high, vary the deposition parameter rising (2.2) and/or the regime of the thermal treatment (3).</li>
</ol>

<ol>
	<li>Kieback, B., Neubrand, A., Riedel, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Processing+techniques+for+functionally+graded+materials.">Processing techniques for functionally graded materials.</a> Materials Science and Engineering - A. 362 (1-2), 81-106 (2003).</li><li>Mortensen, A., Suresh, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionally+graded+metals+and+metal-ceramic+composites:+Part+1+Processing.">Functionally graded metals and metal-ceramic composites: Part 1 Processing.</a> International Materials Reviews. 40 (6), 239-265 (1995).</li><li>Moya, J. S., S&#225;nchez-Herencia, A. J., Requena, J., Moreno, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionally+gradient+ceramics+by+sequential+slip+casting.">Functionally gradient ceramics by sequential slip casting.</a> Materials Letters. 14 (5), 333-335 (1992).</li><li>Moya, J. S., S&#225;nchez-Herencia, J. A., Bartolom&#233;, J. F., Tanimoto, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Elastic+modulus+in+rigid+Al2O3/ZrO2+ceramic+laminates.">Elastic modulus in rigid Al2O3/ZrO2 ceramic laminates.</a> Scripta Materialia. 37 (7), 1095-1103 (1997).</li><li>Zschippang, E., Mannschatz, A., Klemm, H., Moritz, T., Martin, H. -. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Charakterisierung+und+Verarbeitung+von+Si3N4-SiC-MoSi2-Kompositen+f&#252;r+Heizleiteranwendungen.">Charakterisierung und Verarbeitung von Si3N4-SiC-MoSi2-Kompositen f&#252;r Heizleiteranwendungen.</a> Keramische Zeitschrift. 65 (5), 294-297 (2013).</li><li>Scheithauer, U., Haderk, K., Richter, H. -. J., Petasch, U., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+the+kind+and+amount+of+pore+forming+agents+on+the+thermal+shock+behaviour+of+carbon-free+refractory+components+produced+by+multilayer+technology.">Influence of the kind and amount of pore forming agents on the thermal shock behaviour of carbon-free refractory components produced by multilayer technology.</a> refractories WORLDFORUM. 4 (1), 130-136 (2011).</li><li>Scheithauer, U., Schwarzer, E., Slawik, T., Richter, H. -. J., Moritz, T., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionally+Graded+Materials+Made+by+Water-Based+Multilayer+Technology.">Functionally Graded Materials Made by Water-Based Multilayer Technology.</a> Refractories Worldforum. 8 (2), 95-101 (2016).</li><li>Mannschatz, A., H&#228;rtel, A., M&#252;ller-K&#246;hn, A., Moritz, T., Michaelis, A., Wilde, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Manufacturing+of+Two-colored+Co-sintered+Zirconia+Components+by+Inmold-labelling+and+2C-Injection+Molding,+cfi/Ber.">Manufacturing of Two-colored Co-sintered Zirconia Components by Inmold-labelling and 2C-Injection Molding, cfi/Ber.</a> DKG. 91 (8), (2014).</li><li>Moritz, T., Scheithauer, U., Mannschatz, A., Ahlhelm, M., Abel, J., Schwarzer, E., Pohl, M., M&#252;ller-K&#246;hn, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Material-+and+process+hybridization+for+multifunctional+ceramic+and+glass+components.">Material- and process hybridization for multifunctional ceramic and glass components.</a> Ceramic Applications. 5 (2), 66-71 (2017).</li><li>Homa, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rapid+Prototyping+of+high-performance+ceramics+opens+new+opportunities+for+the+CIM+industry.">Rapid Prototyping of high-performance ceramics opens new opportunities for the CIM industry.</a> Powder Injection Moulding International. 6 (3), 65-68 (2012).</li><li>Chartier, T., Badev, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rapid+Prototyping+of+Ceramics.">Rapid Prototyping of Ceramics.</a> Handbook of Advanced Ceramics Elsevier. , (2013).</li><li>Travitzky, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Additive+Manufacturing+of+ceramic-based+materials.">Additive Manufacturing of ceramic-based materials.</a> Advanced Engineering Materials. 16, 729-754 (2014).</li><li>Zocca, A., Colombo, P., Gomes, C. M., G&#252;nster, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Additive+Manufacturing+of+Ceramics:+Issues,+Potentialities,+and+Opportunities.">Additive Manufacturing of Ceramics: Issues, Potentialities, and Opportunities.</a> Journal of the American Ceramic Society. 98 (7), 1983-2001 (2015).</li><li>Scheithauer, U., Schwarzer, E., Richter, H. J., Moritz, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermoplastic+3D+Printing+-+An+Additive+Manufacturing+Method+for+Producing+Dense+Ceramics.">Thermoplastic 3D Printing - An Additive Manufacturing Method for Producing Dense Ceramics.</a> JACT. 12 (1), 26-31 (2014).</li><li>Scheithauer, U., Bergner, A., Schwarzer, E., Richter, H. -. J., Moritz, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Studies+on+thermoplastic+3D+printing+of+steel-zirconia+composites.">Studies on thermoplastic 3D printing of steel-zirconia composites.</a> J Mat Res. 29 (17), 1931-1940 (1931).</li><li>Scheithauer, U., Slawik, T., Schwarzer, E., Richter, H. -. J., Moritz, T., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Additive+Manufacturing+of+Metal-Ceramic-Composites+by+Thermoplastic+3D-Printing.">Additive Manufacturing of Metal-Ceramic-Composites by Thermoplastic 3D-Printing.</a> J. Ceram. Sci. Tech. 06 (02), 125-132 (2015).</li><li>Scheithauer, U., Schwarzer, E., Haertel, A., Richter, H. J., Moritz, T., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Processing+of+thermoplastic+suspensions+for+Additive+Manufacturing+of+Ceramic-+and+Metal-Ceramic-Composites+by+Thermoplastic+3D-Printing+(T3DP),+11th+International+Conference+on+Ceramic+Materials+and+Components+for+Energy+and+Environmental+Applications.">Processing of thermoplastic suspensions for Additive Manufacturing of Ceramic- and Metal-Ceramic-Composites by Thermoplastic 3D-Printing (T3DP), 11th International Conference on Ceramic Materials and Components for Energy and Environmental Applications.</a> Ceramic Transactions. 256, (2016).</li><li>Scheithauer, U., Weingarten, S., Johne, R., Schwarzer, E., Abel, J., Richter, H., Moritz, T., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ceramic-Based+4D-Components:+Additive+Manufacturing+(AM)+of+Ceramic-Based+Functionally+Graded+Materials+(FGM)+by+Thermoplastic+3D-Printing+(T3DP).">Ceramic-Based 4D-Components: Additive Manufacturing (AM) of Ceramic-Based Functionally Graded Materials (FGM) by Thermoplastic 3D-Printing (T3DP).</a> Preprints. , 2017100057 (2017).</li><li>Lee, H. C., Potapova, Y., Lee, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+core-shell+structured,+metal-ceramic+composite+supported+Ru+catalyst+for+methane+steam+reforming.">A core-shell structured, metal-ceramic composite supported Ru catalyst for methane steam reforming.</a> J of Power Sources. 216, 256-260 (2012).</li><li>Molin, S., Tolczyk, M., Gazda, M., Jasinski, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stainless+steel/yttria+stabilized+zirconia+composite+supported+solid+oxide+fuel+cell.">Stainless steel/yttria stabilized zirconia composite supported solid oxide fuel cell.</a> J. Fuel Cell Sci. Technol. 8, 1-5 (2011).</li><li>Roberts, H. W., Berzins, D. W., Moore, B. K., Charlton, D. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metal-Ceramic+Alloys+in+Dentistry:+A+Review.">Metal-Ceramic Alloys in Dentistry: A Review.</a> Journal of Prosthodontics. 18 (2), 188-194 (2009).</li><li>Largiller, G., Bouvard, D., Carry, C. P., Gabriel, A., M&#252;ller, J., Staab, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Deformation+and+cracking+during+sintering+of+bimaterial+components+processed+from+ceramic+and+metal+powder+mixes.+Part+I:+Experimental+investigation.">Deformation and cracking during sintering of bimaterial components processed from ceramic and metal powder mixes. Part I: Experimental investigation.</a> Mechanics of Materials. 53, 123-131 (2012).</li><li>Meulenberg, W. A., Mertens, J., Bram, M., Buchkremer, H. -. P., St&#246;ver, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Graded+porous+TiO2+membranes+for+micro-filtration.">Graded porous TiO2 membranes for micro-filtration.</a> Journal European Ceramic Society. 26, 449-454 (2006).</li><li>Baumann, A., Moritz, T., Lenk, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Multi+component+powder+injection+moulding+of+metal-ceramic-composites.">Multi component powder injection moulding of metal-ceramic-composites.</a> Proceedings of the Euro International Powder Metallurgy Congress and Exhibition. , (2009).</li><li>Scheithauer, U., Johne, R., Weingarten, S., Schwarzer, E., Abel, J., Richter, H., Moritz, T., Michaelis, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Investigation+of+Droplet+Deposition+for+Suspensions+Usable+for+Thermoplastic+3D+Printing+(T3DP).">Investigation of Droplet Deposition for Suspensions Usable for Thermoplastic 3D Printing (T3DP).</a> Journal of Materials Engineering and Performance. , (2017).</li></ol>

The authors have nothing to disclose.

The characterization of the rheological behavior of the molten suspension at high shear rates up to 5000/s is necessary since the assessment of the conditions within the used micro dispensing systems (geometry of piston and nozzle chamber, velocity of piston) revealed that shear rates of 5000/s and higher are generated in the micro dispensing system during the deposition process25.
The investigation of the printing parameters should be done to aid with the calibration of the dispenser for the manufacturing of multi-material components. The influence of the dispenser parameters on the properties of the materials has been discussed in25. Parameter value boundaries have only been determent empirically. Experience so far shows that the variance in droplet chain height and width should not exceed 3 %. Diameter differences up to 100 microns and height differences up to 50 microns can be compensated by the parameters pulse width, droplet fusion factor (DFF) and extrusion width (slicing parameter).
It is critical for the printing process that the layer heights of the different materials are adjusted to each other by changing the distance between the single droplets, since it would result in an unevenness within a layer if the heights of the different materials do not match. An unevenness leads to large defects and faulty components. By reducing the distance between two droplets and the associated greater overlap, the width and height of the droplet chain increases due to the nearly constant volume of the single droplets. It can be observed that the droplet chain width increases faster than the droplet chain height.It is not necessary and probably not possible to realize perfectly shaped hemispheres as single droplets, but you have to make sure by determining the fitting dispensing parameters that the homogeneity of the droplet formation is very high to guarantee a homogenous building of the components.
The measurement at 85 &#176;C simulates the rheological behavior of the suspensions in the feeding cartridge of the micro dispensing system. Above 90 &#176;C, the decomposition of the binder components begins (Figure 7). All suspensions show nearly similar behavior. The used nozzle temperature of the micro dispensing system was 100 &#176;C. This temperature promotes the droplet formation due to the low viscosity caused by increasing the suspensions temperature while passing the nozzle. Because of the short dwell time of the suspensions within the nozzle at this temperature the decomposition is not influencing the material behavior significantly.
The multi-color components could be sintered nearly defect-free, but for the zirconia black - 2 and zirconia white - 2 powders the color of the white phase turned into pink. The cause for the color change are&#160;diffusion processes between the different materials during sintering. This is only an effect at the surface and can be removed by a grinding step. But this is very challenging for complex structures made by AM technologies.
Within the multi-color components&#160;planar and interwoven boundary interfaces developed between the two different compositions. Thus, regardless of the drop-bound deposition of the material, the arrangement of the different microstructures can be realized very precisely. Furthermore, the droplet shape can be exploited to increase the boundary interface between two materials. So far only discrete material transitions have been produced. Future research may also involve the production of gradual changes between materials.

Functionally Graded Materials (FGM) are materials with a variety of properties concerning transitions in the microstructure or in the material1. These transitions can be discrete or continuous. Different kinds of FGM are known, such as components with material gradients, graded porosity as well as multi-colored components.
FGM-components can be manufactured by single conventional shaping technologies2,3,4,5,6,7 or by a combination of these technologies, for example, by in-mold labeling as a combination of tape casting and injection molding8,9.
Additive manufacturing (AM) allows for the production of components with a so far unprecedented freedom of design. This is considered the state of the art shaping technology for polymers and metals. First commercial processes for the processing of&#160;ceramics are available10, and nearly all known AM technologies are used for AM of ceramics in laboratories all over the world11,12,13.
To combine the benefits of AM with the benefits of FGM to ceramic-based 4D components (three dimensions for the geometry and one degree of freedom concerning the material properties at each position) the Thermoplastic 3D-Printing (CerAM -&#160;T3DP) has been developed at Fraunhofer IKTS in Dresden, Germany, as a direct AM technology. This allows the AM of multi-material components14,15,16,17. CerAM -&#160;T3DP is based on the selective deposition of single droplets of particle filled thermoplastic suspensions. By utilizing multiple dosing systems, different thermoplastic suspensions can be deposited beside each other layer by layer to produce bulk material as well as property gradients within the additively manufactured green components18. Unlike indirect AM processes, in which previously deposited materials solidify selectively over the entire layer, the CerAM -&#160;T3DP process does not require the additional effort of removing any non-solidified material prior to the deposition of the next material, making it more suitable for the AM of multi-material components.
Although utilizing the CerAM -&#160;T3DP process allows the AM of FGM and the realization of ceramic-based components with unprecedented properties, there are challenges to overcome regarding the necessary thermal treatment after the AM process, in order to obtain a multi-material composite. In particular, the paired powders in the composite material need to be successfully co-sintered, for which the sintering of the components has to be performed at the same temperature and atmosphere. Therefore, it is a prerequisite for all materials to have a comparable sintering temperature and behavior (starting temperature of sintering, shrinkage behavior). In order to avoid critical mechanical stress during cooling, the coefficient of thermal expansion of all materials has to be approximately equal11.
The combination of materials with different properties in one component opens the door to components with unprecedented properties for manifold applications. E.g. stainless steel-zirconia composites can be used as cutting tools, wear resistant components, energy, and fuel cell components or as bipolar surgical tools19,20,21,22,23,24. Such components could be realized by CerAM -&#160;T3DP14,15,16,17, too, after the adjustment of the sintering behavior by a special milling process16.
Ceramic-based FGM with a graded porosity like dense and porous zirconia combine very good mechanical properties in the dense areas with a high active surface of the porous areas. Such like components can be additively manufactured by CerAM -&#160;T3DP18.
In this paper, we investigate the AM of zirconia components with two different colors in one component by CerAM -&#160;T3DP. We chose white and black zirconia because this combination in one ceramic component is interesting for jewelry applications. The demand of&#160;individualized luxury goods is very high and still growing. Technologies which allow the AM of ceramic-based multi-material components with a high resolution and very good surface properties will allow to satisfy this demand. Ceramics like zirconia are used for example to produce watch components like watch cases and bezels or for rings because of the special haptics, glance, hardness and lower weight compared to metals.

<table><tbody><tr><td>&lt;strong&gt;Material&lt;/strong&gt;</td><td></td><td></td><td></td></tr><tr><td>Zirconia black - 1</td><td>TZ-3Y-Black</td><td>Tosoh</td><td></td></tr><tr><td>Zirconia black - 2</td><td>ZirPro ColorYZ Black</td><td>Saint Gobain</td><td></td></tr><tr><td>Zirconia white - 1</td><td>TZ-3Y-Black</td><td>Tosoh</td><td></td></tr><tr><td>Zirconia white - 2</td><td>ZirPro ColorYZ Arctic White</td><td>Saint Gobain</td><td></td></tr><tr><td>&lt;strong&gt;Equipment&lt;/strong&gt;</td><td></td><td></td><td></td></tr><tr><td>laser diffractometer</td><td>Mastersizer 2000</td><td>Malvern Instruments Ltd., United Kingdom</td><td></td></tr><tr><td>dissolver</td><td>DISPERMAT CA 20-C</td><td>VMA-Getzmann GmbH, Germany</td><td></td></tr><tr><td>rheometer</td><td>Modular Compact Rheometer MCR 302&amp;nbsp;</td><td>Anton Paar, Graz, Austria</td><td></td></tr><tr><td>micro dispensing system</td><td>MDS 3250</td><td>Vermes, Germany&amp;nbsp;&amp;nbsp;</td><td></td></tr><tr><td>T3DP-device&amp;nbsp;</td><td>IKTS-T3DP-device &quot;TRUDE&quot;, in-house development</td><td>Fraunhofer IKTS, not commerzialized</td><td></td></tr><tr><td>profile scanner</td><td>LJ-V7020</td><td>Keyence&amp;nbsp;&amp;nbsp;</td><td></td></tr><tr><td>Slicer 1</td><td>Slic3r</td><td>open source software</td><td></td></tr><tr><td>Slicer 2</td><td>Simplify3D</td><td>Simplofy3D</td><td></td></tr><tr><td>debinding furnace</td><td>NA120/45</td><td>Nabertherm, Germany</td><td></td></tr><tr><td>sintering furnace</td><td>LH 15/12</td><td>Nabertherm, Germany&amp;nbsp;</td><td></td></tr><tr><td>FESEM</td><td>Gemini 982&amp;nbsp;</td><td>Zeiss, Germany&amp;nbsp;</td><td></td></tr></tbody></table>

multi-material ceramic-based components &#8211; additive manufacturing of black-and-white zirconia components by thermoplastic 3d-printing (ceram - t3dp)

To combine the benefits of Additive Manufacturing (AM) with the benefits of Functionally Graded Materials (FGM) to ceramic-based 4D components (three dimensions for the geometry and one degree of freedom concerning the material properties at each position) the Thermoplastic 3D-Printing (CerAM -&#160;T3DP) was developed. It is a direct AM technology which allows the AM of multi-material components. To demonstrate the advantages of this technology black-and-white zirconia components were additively manufactured and co-sintered defect-free.
Two different pairs of black and white zirconia powders were used to prepare different thermoplastic suspensions. Appropriate dispensing parameters were investigated to manufacture single-material test components and adjusted for the additive manufacturing of multi-color zirconia components.

For the production of measured components, only powders of the same manufacturer have been combined for each multi-material component. Experiments with powders of different manufactures in one component are still ongoing. For this purpose, the different shrink rates have to be considered.
The measurement result of the average particle diameter (d50) of the zirconia white - 1 after dispersion was 0.37 &#181;m. The manufacturer states an actual particle size of 0.04 &#181;m (one order of magnitude less). The average particle size (d50) of the zirconia black - 1 is 0.5 &#181;m. Figure 2 (A) shows the FESEM analysis of the zirconia white - 1 and Figure 2 (B) a FESEM-image of the surface of a granulate in detail. Figure 2 (C) and Figure 2 (D) show the same for zirconia black - 1. Both untreated powders consist of big spherical granules (diameter up to 100 &#181;m) which is typical for dry pressing raw materials. The FESEM-images of the granulate surfaces show the primary particles of the zirconia white - 1 (Figure 2 (B)) and zirconia black - 1 (Figure 2 (D)) with an actual particle size of almost 0.04 &#181;m.
The Figure 2 (E) &#8211; 2 (H) show the FESEM-images of the zirconia white - 2 and zirconia black - 2. The measured average particle sizes (d50) of the zirconia powders zirconia white - 2 and zirconia black - 2 are 0.27 &#181;m and 0.25 &#181;m, respectively, wherein the particles are present as spherical granules with diameters up to 100 &#181;m (Figure 2 (E) and Figure 2 (G)). The size of the white powders primary particles is below 0.1 &#181;m (Figure 2 (F)). The black powders primary particles are up to 0.5 &#181;m in diameter (Figure 2 (H)).
Figure 3 (A) shows the dynamic viscosity of the suspensions based on zirconia white - 1 and zirconia black - 1 as a function of the shear rate and in dependence of the temperature (85 &#176;C and 100 &#176;C). Both suspensions show a shear thinning behavior regardless of the temperature.
Table 1 summarizes the measured viscosities of the suspensions at different shear rates and for different temperatures.
Figure 3 (B) shows the rheological behavior of the suspensions based on zirconia white - 2 and zirconia black - 2 (85 &#176;C and 100 &#176;C). All graphs show a shear thinning behavior. Table 2 summarizes the measured viscosities of the suspensions at different shear rates and for different temperatures.
In addition to shear rate-controlled measurements, long-term measurements were carried out. Figure 3 (C) shows the course of the dynamic viscosity during the long-term measurements for all four suspensions at a constant shear rate of 10/s over 2 h. While the dynamic viscosity of the white zirconia suspensions (zirconia white - 1 and zirconia white - 2) is nearly constant (Table 3), the dynamic viscosity tends to decrease slightly of the black zirconia (zirconia black - 1 and zirconia black - 2).
After the empirical determination of the dosing parameters the manufacturing of single component, three dimensional structures became manageable for each suspension. Figure 4 (A) shows a complex sintered test structure based on the suspension made of zirconia white - 1 and additively manufactured by CerAM -&#160;T3DP. The same test structure additively manufactured by CerAM -&#160;T3DP and the zirconia black - 1-suspension is shown in Figure 4 (B).
Figure 4 (C) shows a sintered test structure based on the zirconia suspensions of the zirconia white - 2, Figure 4 (D) a sintered test structure based on zirconia black - 2. Subsequent to the manufacturing of the single-color components the manufacturing of multi-color components took place. The Figure 4 (D) to 4 (F) show some sintered multi-color zirconia components additive manufacturing using the CerAM -&#160;T3DP.
Figure 5 (A) and Figure 5 (B) show FESEM-images of the microstructure of multi-color components with a clearly distinguishable interface between the two suspensions based on the zirconia powders zirconia white - 1 (top) and zirconia black - 1 (bottom).
An energy-dispersive X-ray spectroscopic analysis (EDX) showed that in the microstructure of the sintered&#160;zirconia black - 1 more alumina crust occurs (Figures 6 (A-C)). To evaluate the composition of the and zirconia black - 1-microstructure especially in the dark areas in more detail further EDX investigations took place (Figures 6 (D-G)) which showed the precipitation of alumina (Figure 6 (E)).
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/57538/57538fig1.jpg" /> 
Figure 1: CAD-drawing of used CerAM -&#160;T3DP-device with three micro dispensing units and one surface scanner. <a href="/files/ftp_upload/57538/57538fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/57538/57538fig2.jpg" /> 
Figure 2: FESEM-image of used zirconia granulates. (A) zirconia white - 1 granulates - overview and (B) surface; (C)zirconia black - 1 granulates - overview and (D) surface; (E) zirconia white - 2 granulates - overview and (F) surface; (G) zirconia black - 2 granulates - overview and (H) surface.
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/57538/57538fig3.jpg" /> 
Figure 3: Rheological behavior of thermoplastic suspensions. (A) based on the zirconia powders zirconia white - 1 and zirconia black - 1; (B) based on the zirconia powders zirconia white - 2 and zirconia black - 2; (C) comparison of all four suspensions during a long-term measurement at a constant shear rate of 10/s.
<img alt="Figure 4" class="xfigimg" src="/files/ftp_upload/57538/57538fig4.jpg" /> 
Figure 4: Sintered single- and multi-material test structures additively manufactured by T3DP. (A) based on zirconia white - 1 -suspension; (B) based on zirconia black - 1 -suspension; (C) based on zirconia white - 2 -suspension; (D) based on zirconia black - 2 -suspension; (E) based on zirconia white - 1 - and zirconia black - 1 -suspension; (F) based on zirconia white - 2- and zirconia black - 2 -suspension - frame-like structure and (G) ring-like structure.
<img alt="Figure 5" class="xfigimg" src="/files/ftp_upload/57538/57538fig5.jpg" /> 
Figure 5: FESEM-images. FESEM-images of cross section at interface between sintered zirconia white - 1 (top) and zirconia black - 1 (bottom); (A) planar interface and (B) interwoven interface
<img alt="Figure 6" class="xfigimg" src="/files/ftp_upload/57538/57538fig6.jpg" /> 
Figure 6: Results of EDX measurements at sintered zirconia white - 1 / zirconia black - 1 -interface. (A) Overview about measurement fields 1 + 2 and (D) 3 - 5; results of measurement (B) field 1, (C) field 2, (E) field 3, (F) field 4 and (G) field 5.
<img alt="Figure 7" class="xfigimg" src="/files/ftp_upload/57538/57538fig7.jpg" /> 
Figure 7: Mass change of the zirconia white - 1- and zirconia black - 1 -suspensions during thermal decomposition <a href="/files/ftp_upload/57538/57538fig7large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Table 1" src="/files/ftp_upload/57538/57538table1.jpg" /> 
Table 1: Dynamic viscosity of thermoplastic suspensions based on the zirconia powders zirconia white - 1 and zirconia black - 1. <a href="/files/ftp_upload/57538/Table_01.pdf">Please click here to download this file.</a>
<img alt="Table 2" src="/files/ftp_upload/57538/57538table2.jpg" /> 
Table 2: Dynamic viscosity of thermoplastic suspensions based on the zirconia powders zirconia white - 2 and zirconia black - 2. <a href="/files/ftp_upload/57538/Table_02.pdf">Please click here to download this file.</a>
<img alt="Table 3" src="/files/ftp_upload/57538/57538table3.jpg" /> 
Table 3: Dynamic viscosity of all four suspensions during the long-term measurement at a constant shear rate of 10/s. <a href="/files/ftp_upload/57538/Table_03.pdf">Please click here to download this file.</a>

Watch this Scientific Journal Video about Multi-material Ceramic-Based Components â€“ Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing CerAM - T3DP at Jo

Multi-material Ceramic-Based Components &#8211; Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Here we describe a protocol for additively manufacturing black-and-white zirconia components by Thermoplastic 3D-Printing (CerAM -&#160;T3DP) and co-sintering defect-free.

To combine the benefits of Additive Manufacturing (AM) with the benefits of Functionally Graded Materials (FGM) to ceramic-based 4D components (three ...

multi-material-ceramic-based-components-additive-manufacturing-black

Universidad San Sebastian

Research

JoVE Journal

Engineering

11.3K Views.  Fraunhofer Institute for Ceramic Technologies and Systems IKTS. Here we describe a protocol for additively manufacturing black-and-white zirconia components by Thermoplastic 3D-Printing (CerAM - T3DP) and co-sintering defect-free.

Video: Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Micro 3D Printing Using a Digital Projector and its Application in the Study of Soft Materials Mechanics

Buckling is a classical topic in mechanics. While buckling has long been studied as one of the major structural failure modes1, it has recently drawn new attention as a unique mechanism for pattern transformation. Nature is full of such examples where a wealth of exotic patterns are formed through mechanical instability2-5. Inspired by this elegant mechanism, many studies have demonstrated creation and transformation of patterns using soft materials such as elastomers and hydrogels6-11. Swelling gels are of particular interest because they can spontaneously trigger mechanical instability to create various patterns without the need of external force6-10. Recently, we have reported demonstration of full control over buckling pattern of micro-scaled tubular gels using projection micro-stereolithography (P&mu;SL), a three-dimensional (3D) manufacturing technology capable of rapidly converting computer generated 3D models into physical objects at high resolution12,13. Here we present a simple method to build up a simplified P&mu;SL system using a commercially available digital data projector to study swelling-induced buckling instability for controlled pattern transformation.
A simple desktop 3D printer is built using an off-the-shelf digital data projector and simple optical components such as a convex lens and a mirror14. Cross-sectional images extracted from a 3D solid model is projected on the photosensitive resin surface in sequence, polymerizing liquid resin into a desired 3D solid structure in a layer-by-layer fashion. Even with this simple configuration and easy process, arbitrary 3D objects can be readily fabricated with sub-100 &mu;m resolution.
This desktop 3D printer holds potential in the study of soft material mechanics by offering a great opportunity to explore various 3D geometries. We use this system to fabricate tubular shaped hydrogel structure with different dimensions. Fixed on the bottom to the substrate, the tubular gel develops inhomogeneous stress during swelling, which gives rise to buckling instability. Various wavy patterns appear along the circumference of the tube when the gel structures undergo buckling. Experiment shows that circumferential buckling of desired mode can be created in a controlled manner. Pattern transformation of three-dimensionally structured tubular gels has significant implication not only in mechanics and material science, but also in many other emerging fields such as tunable matamaterials.

We demonstrate controlled pattern transformation of swelling gel tubes by elastic instability. A simple projection micro stereo-lithography setup is built using an off-the-shelf digital data projector to fabricate three-dimensional polymeric structures in a layer-by-layer fashion. Swelling hydrogel tubes under mechanical constraint display various circumferential buckling modes depending on dimension.

Buckling is a classical topic in mechanics. While buckling has long been studied as one of the major structural failure modes1, it has recently drawn new ...

Micro-masonry for 3D Additive Micromanufacturing

Transfer printing is a method to transfer solid micro/nanoscale materials (herein called &#8216;inks&#8217;) from a substrate where they are generated to a different substrate by utilizing elastomeric stamps. Transfer printing enables the integration of heterogeneous materials to fabricate unexampled structures or functional systems that are found in recent advanced devices such as flexible and stretchable solar cells and LED arrays. While transfer printing exhibits unique features in material assembly capability, the use of adhesive layers or the surface modification such as deposition of self-assembled monolayer (SAM) on substrates for enhancing printing processes hinders its wide adaptation in microassembly of microelectromechanical system (MEMS) structures and devices. To overcome this shortcoming, we developed an advanced mode of transfer printing which deterministically assembles individual microscale objects solely through controlling surface contact area without any surface alteration. The absence of an adhesive layer or other modification and the subsequent material bonding processes ensure not only mechanical bonding, but also thermal and electrical connection between assembled materials, which further opens various applications in adaptation in building unusual MEMS devices.

This paper introduces a 3D additive micromanufacturing strategy (termed &#8216;micro-masonry&#8217;) for the flexible fabrication of microelectromechanical system (MEMS) structures and devices. This approach involves transfer printing-based assembly of micro/nanoscale materials in conjunction with rapid thermal annealing-enabled material bonding techniques.

Transfer printing is a method to transfer solid micro/nanoscale materials (herein called &#8216;inks&#8217;) from a substrate where they are generated to ...

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) scaffolds with tunable specific surface areas up to 80 m2&#183;g-1. An aqueous solution of a zirconium salt, yttrium salt, and glucose is mixed with propylene oxide (PO) to form a gel. The gel is dried under ambient conditions to form a xerogel. The xerogel is pressed into pellets and then sintered in an argon atmosphere. During sintering, a YSZ ceramic phase forms and the organic components decompose, leaving behind amorphous carbon. The carbon formed in situ serves as a hard template, preserving a high surface area YSZ nanomorphology at sintering temperature. The carbon is subsequently removed by oxidation in air at low temperature, resulting in a porous, nanostructured YSZ scaffold. The concentration of the carbon template and the final scaffold surface area can be systematically tuned by varying the glucose concentration in the gel synthesis. The carbon template concentration was quantified using thermogravimetric analysis (TGA), the surface area and pore size distribution was determined by physical adsorption measurements, and the morphology was characterized using scanning electron microscopy (SEM). Phase purity and crystallite size was determined using X-ray diffraction (XRD). This fabrication approach provides a novel, flexible platform for realizing unprecedented scaffold surface areas and nanomorphologies for ceramic-based electrochemical energy conversion applications, e.g. solid oxide fuel cell (SOFC) electrodes.

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels

A protocol for fabricating porous, nanostructured yttria-stabilized-zirconia (YSZ) scaffolds at temperatures between 1,000 &#176;C and 1,400 &#176;C is presented.

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) ...

A Soft Tooling Process Chain for Injection Molding of a 3D Component with Micro Pillars

The purpose of this paper is to present the method of a soft tooling process chain employing Additive Manufacturing (AM) for fabrication of injection molding inserts with micro surface features. The Soft Tooling inserts are manufactured by Digital Light Processing (vat photo polymerization) using a photopolymer that can withstand relatively high temperaturea. The part manufactured here has four tines with an angle of 60&#176;. Micro pillars (&#216;200 &#181;m, aspect ratio of 1) are arranged on the surfaces by two rows. Polyethylene (PE) injection molding with the soft tooling inserts is used to fabricate the final parts. This method demonstrates that it is feasible to obtain injection-molded parts with microstructures on complex geometry by additive manufactured inserts. The machining time and cost is reduced significantly compared to conventional tooling processes based on computer numerical control (CNC) machining. The dimensions of the micro features are influenced by the applied additive manufacturing process. The lifetime of the inserts determines that this process is more suitable for pilot production. The precision of the inserts production is limited by the additive manufacturing process as well.

A protocol for fabricating injection molding inserts for complex geometry with micro features on surfaces employing Additive Manufacturing (AM) is presented.

The purpose of this paper is to present the method of a soft tooling process chain employing Additive Manufacturing (AM) for fabrication of injection ...

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Technical ceramics are widely used for industrial and research applications, as well as for consumer goods. Today, the demand for complex geometries with diverse customization options and favorable production methods is increasing continuously. With fused filament fabrication (FFF), it is possible to produce large and complex components quickly with high material efficiency. In FFF, a continuous thermoplastic filament is melted in a heated nozzle and deposited below. The computer-controlled print head is moved in order to build up the desired shape layer by layer. Investigations regarding printing of metals or ceramics are increasing more and more in research and industry. This study focuses on additive manufacturing (AM) with a multi-material approach to combine a metal (stainless steel) with a technical ceramic (zirconia: ZrO2). Combining these materials offers a broad variety of applications due to their different electrical and mechanical properties. The paper shows the main issues in preparation of the material and feedstock, device development, and printing of these composites.

Fused Filament Fabrication FFF of Metal-Ceramic Components

This study shows multi-material additive manufacturing (AM) using fused filament fabrication (FFF) of stainless steel and zirconia.

Technical ceramics are widely used for industrial and research applications, as well as for consumer goods. Today, the demand for complex geometries with ...

Stereolithographic 3D Printing with Renewable Acrylates

The accessibility of cost-competitive renewable materials and their application in additive manufacturing is essential for an efficient biobased economy. We demonstrate the rapid prototyping of sustainable resins using a stereolithographic 3D printer. Resin formulation takes place by straightforward mixing of biobased acrylate monomers and oligomers with a photoinitiatior and optical absorber. Resin viscosity is controlled by the monomer to oligomer ratio and is determined as a function of shear rate by a rheometer with parallel plate geometry. A stereolithographic apparatus charged with the biobased resins is employed to produce complex shaped prototypes with high accuracy. The products require a post-treatment, including alcohol rinsing and UV irradiation, to ensure complete curing. The high feature resolution and excellent surface finishing of the prototypes is revealed by scanning electron microscopy.

A protocol for additive manufacturing with renewable photopolymer resins on a stereolithography apparatus is presented.

The accessibility of cost-competitive renewable materials and their application in additive manufacturing is essential for an efficient biobased economy. ...

Chemistry

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

An additive manufacturing technology is applied to obtain functionally graded ceramic parts. This technology, based on digital light processing/stereolithography, is developed within the scope of the CerAMfacturing European research project. A three-dimensional (3-D) hemi-maxillary bone-like structure is 3-D printed using custom aluminum oxide polymeric mixtures. The powders and mixtures are fully analyzed in terms of rheological behavior in order to ensure proper material handling during the printing process. The possibility to print functionally graded materials using the Admaflex technology is explained in this document. Field-emission scanning electron microscopy (FESEM) show that the sintered aluminum oxide ceramic part has a porosity lower than 1% and no remainder of the original layered structure is found after analysis.

This manuscript describes the processing of single multifunctional ceramic components (e.g., combinations of dense-porous structures) additively manufactured by stereolithography.

An additive manufacturing technology is applied to obtain functionally graded ceramic parts. This technology, based on digital light ...

Negative Additive Manufacturing of Complex Shaped Boron Carbides

Boron carbide (B4C) is one of the hardest materials in existence. However, this attractive property also limits its machineability into complex shapes for high wear, high hardness, and lightweight material applications such as armors. To overcome this challenge, negative additive manufacturing (AM) is employed to produce complex geometries of boron carbides at various length scales. Negative AM first involves gelcasting a suspension into a 3D-printed plastic mold. The mold is then dissolved away, leaving behind a green body as a negative copy. Resorcinol-formaldehyde (RF) is used as a novel gelling agent because unlike traditional hydrogels, there is little to no shrinkage, which allows for extremely complex molds to be used. Furthermore, this gelling agent can be pyrolyzed to leave behind ~50 wt% carbon, which is a highly effective sintering aid for B4C. Due to this highly homogenous distribution of in situ carbon within the B4C matrix, less than 2% porosity can be achieved after sintering. This protocol highlights in detail the methodology for creating near fully dense boron carbide parts with highly complex geometries.

A method called negative additive manufacturing is used to produce near fully dense complex shaped boron carbide parts of various length scales. This technique is possible via the formulation of a novel suspension involving resorcinol-formaldehyde as a unique gelling agent that leaves behind a homogenous carbon sintering aid after pyrolysis.

Boron carbide (B4C) is one of the hardest materials in existence. However, this attractive property also limits its machineability into complex shapes for ...

3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization

3D printing provides facile access to geometrically complex materials. However, these materials have intrinsically linked bulk and interfacial properties dependent on the chemical composition of the resin. In the current work, 3D printed materials are post-functionalized using the 3D printer hardware via a secondary surface-initiated polymerization process, thus providing independent control over the bulk and interfacial material properties. This process begins with preparing liquid resins, which contain a monofunctional monomer, a crosslinking multifunctional monomer, a photochemically labile species that enables initiation of polymerization, and critically, a thiocarbonylthio compound which facilitates reversible addition-fragmentation chain transfer (RAFT) polymerization. The thiocarbonylthio compound, known commonly as a RAFT agent, mediates the chain growth polymerization process and provides polymeric materials with more homogeneous network structures. The liquid resin is cured in a layer-by-layer fashion using a commercially available digital light processing 3D printer to give three-dimensional materials having spatially controlled geometries. The initial resin is removed and replaced with a new mixture containing functional monomers and photoinitiating species. The 3D printed material is then exposed to light from the 3D printer in the presence of the new functional monomer mixture. This allows photoinduced surface-initiated polymerization to occur from the latent RAFT agent groups on the surface of the 3D printed material. Given the chemical flexibility of both resins, this process allows a wide range of 3D printed materials to be produced with tailorable bulk and interfacial properties.

3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization

The present protocol describes the digital light processing-based 3D printing of polymeric materials using type I photoinitiated reversible addition-fragmentation chain transfer polymerization and the subsequent in situ material post-functionalization via surface-mediated polymerization. Photoinduced 3D printing provides materials with independently tailored and spatially controlled bulk and interfacial properties.

3D printing provides facile access to geometrically complex materials. However, these materials have intrinsically linked bulk and interfacial properties ...

Three-dimensional Printing of Thermoplastic Materials to Create Automated Syringe Pumps with Feedback Control for Microfluidic Applications

Microfluidics has become a critical tool in research across the biological, chemical, and physical sciences. One important component of microfluidic experimentation is a stable fluid handling system capable of accurately providing an inlet flow rate or inlet pressure. Here, we have developed a syringe pump system capable of controlling and regulating the inlet fluid pressure delivered to a microfluidic device. This system was designed using low-cost materials and additive manufacturing principles, leveraging three-dimensional (3D) printing of thermoplastic materials and off-the-shelf components whenever possible. This system is composed of three main components: a syringe pump, a pressure transducer, and a programmable microcontroller. Within this paper, we detail a set of protocols for fabricating, assembling, and programming this syringe pump system. Furthermore, we have included representative results that demonstrate high-fidelity, feedback control of inlet pressure using this system. We expect this protocol will allow researchers to fabricate low-cost syringe pump systems, lowering the entry barrier for the use of microfluidics in biomedical, chemical, and materials research.

Here we present a protocol to construct a pressure-controlled syringe pump to be used in microfluidic applications. This syringe pump is made from an&#160;additively manufactured body, off-the-shelf hardware, and open-source electronics. The resulting system is low-cost, straightforward to build, and delivers well-regulated fluid flow to enable rapid microfluidic research.

Microfluidics has become a critical tool in research across the biological, chemical, and physical sciences. One important component of microfluidic ...

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Podsumowanie

Przeglądaj więcej filmów

Micro 3D Printing Using a Digital Projector and its Application in the Study of Soft Materials Mechanics

Micro-masonry for 3D Additive Micromanufacturing

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

A Soft Tooling Process Chain for Injection Molding of a 3D Component with Micro Pillars

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Stereolithographic 3D Printing with Renewable Acrylates

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

Negative Additive Manufacturing of Complex Shaped Boron Carbides

3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization

Three-dimensional Printing of Thermoplastic Materials to Create Automated Syringe Pumps with Feedback Control for Microfluidic Applications