Microcracks can form at the interface between coarse aggregate and cement paste, even before any load is applied.

Up to about 30 percent of the concrete's maximum strength, these cracks remain stable and do not expand.

When the stress exceeds 30 percent of the concrete's maximum strength, the formation of bond cracks, which are microcracks grown in length, width, and frequency at the interfaces between the aggregates and cement paste, are observed.

Bond cracks are reflected by the curvilinear stress-strain curve of concrete, indicating an increase in strain, outpacing the stress.

When concrete reaches 70 to 90 percent of its maximum strength, cracks start to form through the mortar matrix, connecting existing bond cracks and creating a continuous pattern.

Naturally, an increase in the load applied to a material can lead to immediate failure when it reaches its nominal ultimate strength.

Ultrasonic and acoustic emission testing can track the progression of cracks in concrete.

With the development of cracks, there is a noticeable reduction in the transverse ultrasonic pulse velocity and an increase in acoustic emissions, indicating failure.