We would like to acknowledge the FQ-PAIP and DGAPA-PAPIIT programs from National Autonomous University of Mexico (grant numbers 5000-9158, 5000-9156, IA205616 and IA205316) and the National Council for Science and Technology from Mexico -CONACYT- (grant number 251533).

Caution: Please consult all relevant material safety data sheets (MSDS) before use. Several of the chemicals used in this protocol are acutely toxic and carcinogenic. Carbon nanotube derivatives may have additional respiratory hazards compared to other traditional bulk carbon allotropes. It is suspected that carbon nanotubes in aerosol may affect lungs in a similar way than asbestos, though their carcinogenic properties have not been completely elucidated so far. Please use all appropriate safety practices when performing the chemical reactions and product processing steps including the use of fume hood and personal protective equipment (lab coat, gloves, safety glasses, closed shoes, full length pants) while suitable filtering facepiece respirators should be particularly used when potential nanotube dust may be generated (NIOSH approved N95 model, or European EN 149 certified FFP3 versions). Portions of the following procedure involve standard inert atmosphere handling techniques.24
1. Selective Hydroxylation of Multiwalled Carbon Nanotubes 22
<ol>
	<li>Biphasic Catalytically Mediated Oxidation of MWCNTs
	<ol>
		<li>Preparation of the Organic Phase
		<ol>
			<li>Add 2.5 g of pristine MWCNTs to a watch glass, Petri dish or beaker.</li>
			<li>Move the container into an 80 &#176;C vacuum oven and cover with a suitable watch glass. Turn on the vacuum pump of the oven and set the system to ca. 200 mmHg.</li>
			<li>Dry the nanotubes in the vacuum oven for 12 h. After this step, the water content in the MWCNTs will be eliminated.</li>
			<li>Pour the dried MWCNTs into a 100 mL round bottom flask with a glass funnel and a spatula and remove the funnel once finished.</li>
			<li>Introduce a magnetic stirring bar to the round bottom flask and add ~ 50 mL of 99% dichloromethane into the flask using a beaker. Stir at 60 rpm using a stirring plate until agglomerates disappear.</li>
			<li>If agglomerates remain in solution after stirring for 10 min, move the flask into an ultrasonic bath and turn on the system for 5 min. Repeat sonication if necessary. This solution will be the organic phase in the oxidation reaction stage.</li>
		</ol>
		</li>
		<li>Preparation of the Aqueous Phase
		<ol>
			<li>In a 25 mL beaker, dissolve 0.6 g of tetrapropylammonium bromide (TPABr) in 5 mL of distilled water using a magnetic stirring bar and a stirring plate.</li>
			<li>In a 10 mL volumetric flask, dissolve 0.253 g KMnO4 in distilled water (0.16 M solution) and keep the solution in a beaker at hand. This solution will be used in Step 1.1.2.4.</li>
			<li>Take 5 mL of glacial acetic acid (HOAc) and transfer the volume drop-wise to the TPABr solution. Using a graduated pipette and constant stirring in an ice bath may be helpful. 
			NOTE: The mixture process is exothermic, therefore, the addition should be carried out slowly to avoid possible injuries by projected droplets or an excessive warming.</li>
			<li>Transfer a 5 mL aliquot of the 0.16 M KMnO4 aqueous solution to the acidified TPABr solution. Using a clean graduated pipette and stirring may be helpful.</li>
			<li>Keep the previous solution covered with a watch glass until needed. This solution will be the aqueous phase in the oxidation reaction stage.</li>
		</ol>
		</li>
		<li>Oxidation Reaction
		<ol>
			<li>Pour the aqueous phase into the round bottom flask that contains the organic phase. This mixture will be the biphasic reaction mixture.</li>
			<li>Using the stirring plate, agitate the biphasic system at 80 rpm or more and leave the mixture under stirring at room temperature for 24 h. After this time, the violet aqueous phase turns pale pink and the nanotubes become hydroxylated (MWCNT-OH).</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Purification of MWCNT-OH
	<ol>
		<li>Liquid-Liquid Extraction
		<ol>
			<li>Transfer the biphasic reaction mixture to a 150 mL or 200 mL separatory funnel with the stopcock at the closed position. Use a glass funnel and a spatula if needed.</li>
			<li>Using a Beral pipette, a Pasteur pipette with a rubber bulb attached or a beaker, add ~ 0.25 mL of concentrated hydrochloric acid into the separatory funnel.</li>
			<li>Use the separatory funnel.
			<ol>
				<li>Close the separatory funnel with a Teflon stopper (do not use glass stoppers for carbon nanotubes) and agitate vigorously for 5 s in a fume hood with the sash window down. During agitation, always hold the stopper strongly attached to the funnel with one hand and grab the stopcock with the other hand.</li>
				<li>Immediately after the agitation step, turn the funnel upside down and release the pressure build-up by opening the stopcock with the respective hand. 
				NOTE: Make sure to address the pressure direction to the rear of the fume food.</li>
				<li>Repeat the last two agitation/pressure-release steps in cycles of 3 - 5.</li>
				<li>Once the last cycle is finished, immediately remove the stopper and leave the funnel clamped and undisturbed until phase separation is evident. After liquid-liquid separation, the aqueous phase remains above the organic phase. The MWCNT-OH will remain at the organic phase.</li>
			</ol>
			</li>
			<li>If no phase separation occurs, add 1 - 5 mL of brine (10 - 20% NaCl in water, m/v) to the separatory funnel using a Beral pipette or a Pasteur pipette, mix gently and leave the mixture undisturbed until phase separation. Repeat until needed.</li>
			<li>Recover the organic phase on a 150 mL beaker keeping the stopcock open until the phase boundary reaches the stopcock position. A 150 mL Erlenmeyer flask can be alternatively used to recover the organic phase; however, retrieval of nanotubes from this container type is usually more difficult.</li>
			<li>Keep the recovered solution protected with a watch glass until filtration.</li>
			<li>Discard the aqueous phase appropriately.</li>
		</ol>
		</li>
		<li>Setting of the Vacuum Filtration System
		<ol>
			<li>Set the vacuum filtration system seating the stopper and base firmly into the neck of a clamped Kitasato flask.</li>
			<li>Keep a 47 mm diameter membrane filter at hand and, depending on the membrane material and indications from the manufacturer, optionally follow this step and the next two ones (Steps 1.2.2.2 - 1.2.2.4). Prepare a 100 mm diameter Petri dish with ethanol (EtOH) filling 50% of its capacity.</li>
			<li>With smooth-tip forceps, place the 47 mm diameter membrane filter on the Petri dish with EtOH. Leave the membrane in EtOH for 2 - 5 min. Make sure to use a membrane with a pore size 0.45 - 20 &#181;m. Smaller pore sizes will clog the filtration, while larger ones will reduce filtering efficiency.</li>
			<li>Remove the membrane from the EtOH using the smooth-tip forceps.</li>
			<li>Center the membrane on the sintered glass area of the filter support surface starting by the edge of the membrane. The optional wetting with EtOH may facilitate this step.</li>
			<li>Center the flange of the funnel on top of the assembly. Do not disturb the membrane. Lock the funnel and base together with the spring clamp.</li>
			<li>Connect the system to the vacuum source. Do not turn the vacuum on until needed.</li>
		</ol>
		</li>
		<li>Filtration of the MWCNT-OH
		<ol>
			<li>Pour the retrieved organic phase into the vacuum filtration funnel aided by a glass rod. Apply vacuum to filter the sample until dryness.</li>
			<li>Wash the solid with 40 - 50 mL of 95% methanol (MeOH) using a wash bottle. Using a glass rod may be helpful in this task. Repeat this process at least 5 times. Keep the vacuum on during this step.</li>
			<li>After washing, leave the system under vacuum for 20 min covered with a glass watch to dry the solid.</li>
			<li>In order to recover the solid from the membrane, follow the next Steps 1.2.3.5 - 1.2.3.8.</li>
			<li>Carefully, remove the spring clamp, then vertically remove the funnel without disturbing the membrane and the solid.</li>
			<li>Very carefully, remove the membrane together with the solid from the filter support surface aided by a spatula and the smooth-tip forceps.</li>
			<li>Transfer the membrane with the solid to a 100 mm diameter Petri dish or watch glass.</li>
			<li>Aided by two smooth-tip forceps and a spatula, recover the solid from the membrane surface until all the product is deposited on the Petri dish/watch glass.</li>
		</ol>
		</li>
		<li>Drying and Storage of MWCNT-OH
		<ol>
			<li>Cover the Petri dish/watch glass with a suitable watch glass (larger diameter is required). 
			NOTE: Do not use sealing film to avoid electrostatic charging.</li>
			<li>Introduce the Petri dish/watch glass into a vacuum oven heated at 80 &#176;C. Turn on the vacuum pump of oven and set the system to ca. 200 mm Hg.</li>
			<li>Dry the solid for 24 h. After this step, the solvent content in the product will be eliminated. If the product will not be used immediately, store the solid in a desiccator until needed.</li>
		</ol>
		</li>
	</ol>
	</li>
</ol>
2. Grafting MWCNT-OH with Polystyrene Chains 22,23
<ol>
	<li>Modification of MWCNT-OH with Silylated Methacrylic Moieties
	<ol>
		<li>Pour 2.5 g MWCNT-OH and 5 g of hydroquinone into a clean 100 mL Schlenk flask using a glass funnel and a spatula, remove the funnel and introduce a magnetic stirring bar.</li>
		<li>Set the Schlenk flask into reflux mode according to the following indications:
		<ol>
			<li>Connect the Schlenk flask to the vacuum/inert gas manifold system using a suitable rubber tubing attached to the flask&#39;s glass joint. Keep the flask&#39;s manifold closed.</li>
			<li>Connect a suitable condenser to the tap water system using suitable rubber tubing, making sure to set the water income through the glass joint closest to the male joint.</li>
			<li>Lubricate the male joint of the condenser with an evenly applied fine layer of vacuum grease. 
			NOTE: The joint should not be over-greased to avoid product contamination.</li>
			<li>Attach the condenser&#39;s male joint to the Schlenk flask&#39;s neck. Close the condenser&#39;s female joint with a rubber stopper.</li>
			<li>Carefully, open the flask to the vacuum. Make sure that the nanotubes are not sucked up into the vacuum line during this process.</li>
			<li>Fill the Schlenk flask with N2 gas.</li>
			<li>Repeat the last two steps two more times.</li>
			<li>Keep the system under positive N2 gas flow.</li>
		</ol>
		</li>
		<li>Aided by a clean cannula and a suitable syringe, slowly inject 50 mL dry toluene through the rubber stopper.</li>
		<li>Using the stirring plate and a thermal bath, agitate the mixture vigorously at 80 rpm or more and leave the mixture under stirring for 5 - 10 min at room temperature.</li>
		<li>Using a clean cannula and a syringe, inject 5 mL of TMSPMA through the rubber stopper.</li>
		<li>Set the temperature to 100 &#176;C and leave the reaction under reflux and stirring for 12 h. After this time, silylated methacrylic moieties are chemically couple to the hydroxyl groups on the MWCNTs (namely MWCNT-O-TMSPMA).</li>
		<li>Once the reaction is over, carefully remove the rubber stopper, close the N2 flow and wait until the flask is at room temperature.</li>
		<li>Set a vacuum filtration system (Step 1.2.2).</li>
		<li>Filter the solid (Step 1.2.3). Wash with MeOH in excess.</li>
		<li>Dry and store the MWCNT-O-TMSPMA (Step 1.2.4).</li>
	</ol>
	</li>
	<li>Polymerization of Styrene on Modified MWCNTs
	<ol>
		<li>Pour 2.5 g of the MWCNT-O-TMSPMA and 75 mg of azobisisobutyronitrile (AIBN) into a clean 100 mL Schlenk flask using a glass funnel and a spatula and remove the funnel. 
		Caution: AIBN powder should not be exposed to heat or strongly oxidizing agents, as it may spontaneously explode.</li>
		<li>Introduce a magnetic stirring bar to the Schlenk flask.</li>
		<li>Set the Schlenk flask into reflux mode (Step 2.1.2).</li>
		<li>Using a clean cannula and a syringe, inject 50 mL dry toluene through the rubber stopper.</li>
		<li>Using the stirring plate and the thermal bath, agitate the mixture at 80 rpm or more and leave the mixture under stirring for 5 - 10 min at room temperature.</li>
		<li>Aided by a clean cannula and a syringe, inject 7.5 mL of styrene through the stopper.</li>
		<li>Set the temperature to 70 &#176;C and leave the reaction under reflux, stirring and N2 for 12 h. After this time, PS chains are grafted to the nanotube sidewalls (MWCNT-O-PS).</li>
		<li>Open the system to the air, close the N2 flow and cool the flask to room temperature.</li>
		<li>Set a vacuum filtration system (Step 1.2.2).</li>
		<li>Filter and wash the solid (Step 1.2.3). Use acetone instead of MeOH during the washing step. Wash the solid five times more with 20 mL THF to remove unbound polystyrene.</li>
		<li>Dry and store the MWCNT-O-PS (Step 1.2.4). 
		NOTE: The length of the polymer chain grafted to the nanotubes can be tuned by changing the concentration of styrene in toluene during the polymerization step; lower concentrations produce shorter chains. The polymerization reaction time can be used to adjust the polymer chain size; shorter reaction times reduce the length of the chains. See references 22 and 23 for details.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Iijima, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Helical+Microtubules+of+Graphitic+Carbon.">Helical Microtubules of Graphitic Carbon.</a> Nature. 354, 56-58 (1991).</li><li>Iijima, S., Ichihashi, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Single-Shell+Carbon+Nanotubes+of+1-nm+Diameter.">Single-Shell Carbon Nanotubes of 1-nm Diameter.</a> Nature. 363, 603-605 (1993).</li><li>Dai, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+Nanotubes:+Synthesis,+Integration+and+Properties.">Carbon Nanotubes: Synthesis, Integration and Properties.</a> Acc. Chem. Res. 35, 1035-1044 (2002).</li><li>Karousis, N., Tagmatarchis, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Current+Progress+on+the+Chemical+Modification+of+Carbon+Nanotubes.">Current Progress on the Chemical Modification of Carbon Nanotubes.</a> Chem. Rev. 110, 5366-5397 (2010).</li><li>Zhao, Y. L., Stoddart, J. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Noncovalent+Functionalization+of+Single-Walled+Carbon+Nanotubes.">Noncovalent Functionalization of Single-Walled Carbon Nanotubes.</a> Acc. Chem. Res. 42, 1161-1171 (2009).</li><li>Zelada-Guill&#233;n, G. A., Riu, J., D&#252;zg&#252;n, A., Rius, F. X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immediate+Detection+of+Living+Bacteria+at+Ultralow+Concentrations+Using+a+Carbon+Nanotube+Based+Potentiometric+Aptasensor.">Immediate Detection of Living Bacteria at Ultralow Concentrations Using a Carbon Nanotube Based Potentiometric Aptasensor.</a> Angew. Chem. Int. Ed. 48, 7334-7337 (2009).</li><li>Zelada-Guill&#233;n, G. A., Blondeau, P., Rius, F. X., Riu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+Nanotube-Based+Aptasensors+for+the+Rapid+and+Ultrasensitive+Detection+of+Bacteria.">Carbon Nanotube-Based Aptasensors for the Rapid and Ultrasensitive Detection of Bacteria.</a> Methods. 63, 233-238 (2013).</li><li>Jung, Y., Li, X., Rajan, N. K., Taylor, A. D., Reed, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Record+High+Efficiency+Single-Walled+Carbon+Nanotube/Silicon+p-n+Junction+Solar+Cells.">Record High Efficiency Single-Walled Carbon Nanotube/Silicon p-n Junction Solar Cells.</a> Nano Lett. 13, 95-99 (2013).</li><li>Esc&#225;rcega-Bobadilla, M. V., Rodr&#237;guez-P&#233;rez, L., Teuma, E., Serp, P., Masdeu-Bult&#243;, A. M., G&#243;mez, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rhodium+Complexes+Containing+Chiral+P-Donor+Ligands+as+Catalysts+for+Asymmetric+Hydrogenation+in+Non+Conventional+Media.">Rhodium Complexes Containing Chiral P-Donor Ligands as Catalysts for Asymmetric Hydrogenation in Non Conventional Media.</a> Chem. Soc. Rev. 141, 808-816 (2011).</li><li>Miners, S. A., Rance, G. A., Khlobystov, A. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Chemical+Reactions+Confined+within+Carbon+Nanotubes.">Chemical Reactions Confined within Carbon Nanotubes.</a> Chem. Soc. Rev. 45, 4727-4746 (2016).</li><li>Rege, K., Raravikar, N. R., Kim, D. Y., Schadler, L. S., Ajayan, P. M., Dordick, J. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Enzyme-Polymer-Single+Walled+Carbon+Nanotube+Composites+as+Biocatalytic+Films.">Enzyme-Polymer-Single Walled Carbon Nanotube Composites as Biocatalytic Films.</a> Nano Lett. 3, 829-832 (2003).</li><li>Ma, R., Menamparambath, M. M., Nikolaev, P., Baik, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transparent+Stretchable+Single-Walled+Carbon+Nanotube-Polymer+Composite+Films+with+Near-Infrared+Fluorescence.">Transparent Stretchable Single-Walled Carbon Nanotube-Polymer Composite Films with Near-Infrared Fluorescence.</a> Adv. Mater. 25, 2548-2553 (2013).</li><li>De Volder, M. F. L., Tawfick, S. H., Baughman, R. H., Hart, A. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+Nanotubes:+Present+and+Future+Commercial+Applications.">Carbon Nanotubes: Present and Future Commercial Applications.</a> Science. 339, 535-539 (2013).</li><li>Lehn, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Perspectives+in+Chemistry+-+Steps+towards+Complex+Matter.">Perspectives in Chemistry - Steps towards Complex Matter.</a> Angew. Chem. Int. Ed. 52, 2836-2850 (2013).</li><li>Mattia, E., Otto, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Supramolecular+Systems+Chemistry.">Supramolecular Systems Chemistry.</a> Nat. Nanotechnol. 10, 111-119 (2015).</li><li>Leh, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Supramolecular Chemistry: Concepts and Perspectives. , (1995).</li><li>Esc&#225;rcega-Bobadilla, M. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanorings+and+Rods+Interconnected+by+Self-Assembly+Mimicking+an+Artificial+Network+of+Neurons.">Nanorings and Rods Interconnected by Self-Assembly Mimicking an Artificial Network of Neurons.</a> Nat. Commun. 4, 2648 (2013).</li><li>Gegenhuber, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Noncovalent+Grafting+of+Carbon+Nanotubes+with+Triblock+Terpolymers:+Toward+Patchy+1D+Hybrids.">Noncovalent Grafting of Carbon Nanotubes with Triblock Terpolymers: Toward Patchy 1D Hybrids.</a> Macromolecules. 48, 1767-1776 (2015).</li><li>Peng, H., Alemany, L. B., Margrave, J. L., Khabashesku, V. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sidewall+Carboxylic+Acid+Functionalization+of+Single-Walled+Carbon+Nanotubes.">Sidewall Carboxylic Acid Functionalization of Single-Walled Carbon Nanotubes.</a> J. Am. Chem. Soc. 125, 15174-15182 (2003).</li><li>Furtado, C. A., Kim, U. J., Gutierrez, H. R., Pan, L., Dickey, E. C., Ecklund, P. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Debundling+and+Dissolution+of+Single-Walled+Carbon+Nanotubes+in+Amide+Solvents.">Debundling and Dissolution of Single-Walled Carbon Nanotubes in Amide Solvents.</a> J. Am. Chem. Soc. 126, 6095-6105 (2004).</li><li>Jeon, J. H., Lim, J. H., Kim, K. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+Hybrid+Nanocomposites+with+Polystyrene+and+Multiwalled+Carbon+Nanotubes+with+Well-Defined+Polystyrene+via+Multiple+Atom+Transfer+Radical+Polymerization.">Fabrication of Hybrid Nanocomposites with Polystyrene and Multiwalled Carbon Nanotubes with Well-Defined Polystyrene via Multiple Atom Transfer Radical Polymerization.</a> Polymer. 50, 4488-4495 (2009).</li><li>Kim, M., Hong, C. K., Choe, S., Shim, S. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Polystyrene+Brush+on+Multiwalled+Carbon+Nanotubes+Treated+with+KMnO4+in+the+Presence+of+a+Phase-Transfer+Catalyst.">Synthesis of Polystyrene Brush on Multiwalled Carbon Nanotubes Treated with KMnO4 in the Presence of a Phase-Transfer Catalyst.</a> J. Polym. Sci. Pol. Chem. 45, 4413-4420 (2007).</li><li>Oliveira, E. Y. S., Bode, R., Esc&#225;rcega-Bobadilla, M. V., Zelada-Guill&#233;n, G. A., Maier, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polymer+Nanocomposites+from+Self-Assembled+Polystyrene-Grafted+Carbon+Nanotubes.">Polymer Nanocomposites from Self-Assembled Polystyrene-Grafted Carbon Nanotubes.</a> New J. Chem. 40, 4625-4634 (2016).</li><li>Shriver, D. F., Drezdzon, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> The Manipulation of Air-Sensitive Compounds. , (1986).</li><li>Bressy, C., Ngo, V. G., Ziarelli, F., Margaillan, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=New+Insights+into+the+Adsorption+of+3-(Trimethoxysilyl)-propylmethacrylate+on+Hydroxylated+ZnO+Nanopowders.">New Insights into the Adsorption of 3-(Trimethoxysilyl)-propylmethacrylate on Hydroxylated ZnO Nanopowders.</a> Langmuir. 28, 3290-3297 (2012).</li><li>Wu, X., Qiu, J., Liu, P., Sakai, E., Lei, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polystyrene+Grafted+Carbon+Black+Synthesis+via+in+situ+Solution+Radical+Polymerization+in+Ionic+Liquid.">Polystyrene Grafted Carbon Black Synthesis via in situ Solution Radical Polymerization in Ionic Liquid.</a> J. Polym. Res. 20, 167 (2013).</li></ol>

The authors have nothing to disclose.

In this method, there are some steps which result critical to guarantee a successful grafting process. First, the biphasic catalytically mediated oxidation reaction (Step 1.1) should be carried out with recently dispersed carbon nanotubes (Step 1.1.1.5). If dispersion results unviable according to the recommendations in the protocol, the use of an ultrasonic tip sonicator would be helpful if using the same indications (Step 1.1.1.6). Using shorter MWCNTs may also help in solving dispersion issues. Second, setting of the ...

Since the discovery of single-walled carbon nanotubes (SWCNTs),1,2 the scientific communities have applied their outstanding electrical, mechanical and thermal properties3 in a wide range of cutting-edge applications by modulating their surface properties via covalent4 and non-covalent5 strategies. Examples of those applications include their use as transducers in sensors,6,7 electrodes in solar cells,8 heterogeneous supports in catalysis,9 nanoreactors in synthesis,10 anti-fouling agents in protective films,11 fillers in composite materials,12etc. However, the possibility to modulate the surface properties of their more robust, yet industrially available multiwalled counterparts namely, MWCNTs, to control the directionality in their non-covalent interactions at the nanoscale, has remained a difficult task so far.13
Supramolecular self-assembly of molecular building blocks is one of the most versatile strategies to control the organization of matter at the nanoscale.14,15 In this sense, supramolecular interactions involve directional, short-range and mid-range non-covalent interactions such as H-bond, Van der Waals, dipole-dipole, ion-dipole, dipole-induced dipole, &#960;- &#960; stacking, cation-&#960;, anion-&#960;, coulombic, among others.16 Unfortunately, directionality in self-assembly for larger structures such as MWCNTs is not spontaneous and usually requires external motive forces (e.g. templates or energy dissipation systems).17 A recent report used non-covalent wrapping of nanotubes with tailored co-polymers to pursue the latter goal,18 but the use of covalent strategies to offer new alternatives to solve that problem have remained scarcely explored.
Chemical modification of carbon nanotubes can be selectively carried out to introduce different functional groups either to the termini or to the sidewalls of the same.19,20 One of the most useful approaches to tailor the surface properties in carbon nanostructures is polymer-grafting through standard polymerization routes. Typically, those approaches involve the preliminary introduction of polymerizable or initiator groups (acrylic, vinyl, etc.) on the nanostructure surface and their successive polymerization with a suitable monomer.21 In the case of MWCNTs, the covalent introduction of polymer chains on the sidewalls to control their patchiness in an anisotropic fashion has remained a challenge.
Here we will show how a series of straightforward chemical modification steps22,23 can be applied to insert PS chains on the sidewalls of MWCNTs in order to modify their surface patchiness and to promote their anisotropic self-assembly23 at the nanoscale. During the modification route, a first step allows for the selective hydroxylation of pristine MWCNTs at the sidewalls by following a biphasic catalytically mediated oxidation reaction to yield the hydroxylated counterparts namely, MWCNT-OH. A second step uses 3-(trimethoxysilyl)propyl methacrylate (TMSPMA) to introduce silylated methacrylic moieties to the previously created hydroxyl groups (MWCNT-O-TMSPMA). These inserts will provide surface reactive sites during a third step, when styrene monomer is polymerized from the methacrylic moieties thus yielding polymer chains grafted to the sidewalls of the nanotubes at the end (i.e. MWCNT-O-PS).

<table><tbody><tr><td>Tetrapropylammonium bromide, 99 % (TPABr)</td><td>Sigma-Aldrich</td><td>88104</td><td>Irritant, toxic</td></tr><tr><td>Potassium permanganate, 99 % (KMnO&lt;sub&gt;4&lt;/sub&gt;)</td><td>Sigma-Aldrich</td><td>223468</td><td></td></tr><tr><td>Acetic acid, 99.5 %</td><td>Sigma-Aldrich</td><td>45726</td><td></td></tr><tr><td>Pristine multiwalled carbon nanotubes, 99 % (MWCNTs)</td><td>Bayer Technology Services</td><td>Donated sample</td><td>Harmful dusts. &gt;1 micrometer in length and 13&amp;ndash;16 nm in outer diameter. Alternative supplier: Nanocyl, Catalog N. NC7000, website: http://www.nanocyl.com/</td></tr><tr><td>Sodium Chloride, 98 % (NaCl)</td><td>Sigma-Aldrich</td><td>S3014</td><td>Technical grade can also be used</td></tr><tr><td>Ethanol, 99.8 % (EtOH)</td><td>Sigma-Aldrich</td><td>32221</td><td>Technical grade can also be used</td></tr><tr><td>Methanol, 99.8 % (MeOH)</td><td>Sigma-Aldrich</td><td>322415</td><td>Highly toxic. Technical grade can also be used</td></tr><tr><td>Hydroquinone, 99 %</td><td>Sigma-Aldrich</td><td>H9003</td><td></td></tr><tr><td>Toluene, 99.8 %</td><td>Sigma-Aldrich</td><td>244511</td><td>Anhydrous</td></tr><tr><td>3-(Trimethoxysilyl)propyl methacrylate, 98 % (TMSPMA)</td><td>Sigma-Aldrich</td><td>440159</td><td>Air sensitive, toxic</td></tr><tr><td>Azobisisobutyronitrile, 99 % (AIBN)</td><td>Sigma-Aldrich</td><td>755745</td><td>Explosive</td></tr><tr><td>Styrene, 99 %</td><td>Sigma-Aldrich</td><td>S4972</td><td>Purified using an alumina gel preparative column and stored at 4 &amp;deg;C</td></tr><tr><td>Acetone, 99.5 %</td><td>Sigma-Aldrich</td><td>179124</td><td>Technical grade can also be used</td></tr><tr><td>Tetrahydrofuran, 99.9 % (THF)</td><td>Sigma-Aldrich</td><td>494461</td><td></td></tr><tr><td>Dichloromethane, 99.5 %</td><td>Sigma-Aldrich</td><td>443484</td><td>Highly toxic</td></tr><tr><td>Hydrochloric acid, 37 %</td><td>Sigma-Aldrich</td><td>435570</td><td>Harmful fumes</td></tr></tbody></table>

grafting multiwalled carbon nanotubes with polystyrene to enable self-assembly and anisotropic patchiness

We demonstrate a straightforward protocol to graft pristine multiwalled carbon nanotubes (MWCNTs) with polystyrene (PS) chains at the sidewalls through a free-radical polymerization strategy to enable the modulation of the nanotube surface properties and produce supramolecular self-assembly of the nanostructures. First, a selective hydroxylation of the pristine nanotubes through a biphasic catalytically mediated oxidation reaction creates superficially distributed reactive sites at the sidewalls. The latter reactive sites are subsequently modified with methacrylic moieties using a silylated methacrylic precursor to create polymerizable sites. Those polymerizable groups can address further polymerization of styrene to produce a hybrid nanomaterial containing PS chains grafted to the nanotube sidewalls. The polymer-graft content, amount of silylated methacrylic moieties introduced and hydroxylation modification of the nanotubes are identified and quantified by Thermogravimetric Analysis (TGA). The presence of reactive functional groups hydroxyl and silylated methacrylate are confirmed by Fourier Transform Infrared Spectroscopy (FT-IR). Polystyrene-grafted carbon nanotube solutions in tetrahydrofuran (THF) provide wall-to-wall collinearly self-assembled nanotubes when cast samples are analyzed by transmission electron microscopy (TEM). Those self-assemblies are not obtained when suitable blanks are similarly cast from analogous solutions containing non-grafted counterparts. Therefore, this method enables the modification of the nanotube anisotropic patchiness at the sidewalls which results into spontaneous auto-organization at the nanoscale.

TGA data were collected from pristine nanotubes, hydroxylated nanotubes, nanotubes modified with silylated methacrylic moieties and polystyrene-grafted nanotubes (Figure 1). FT-IR results were collected from hydroxylated nanotubes and nanotubes modified with silylated methacrylic moieties (Figure 2). TEM images were collected from pristine nanotubes and polystyrene-grafted nanotubes (Figure 3). TGA d...

Watch this Scientific Journal Video about Grafting Multiwalled Carbon Nanotubes with Polystyrene to Enable Self-Assembly and Anisotropic Patchiness at JoVE.com

Grafting Multiwalled Carbon Nanotubes with Polystyrene to Enable Self-Assembly and Anisotropic Patchiness

A procedure for the synthesis of polystyrene-grafted multiwalled carbon nanotubes using successive chemical modification steps to selectively introduce the polymer chains to the sidewalls and their self-assembly via anisotropic patchiness is presented.

We demonstrate a straightforward protocol to graft pristine multiwalled carbon nanotubes (MWCNTs) with polystyrene (PS) chains at the sidewalls through a ...

grafting-multiwalled-carbon-nanotubes-with-polystyrene-to-enable-self

Universidad San Sebastian

Research

JoVE Journal

Chemistry

8.0K Views.  National Autonomous University of Mexico. A procedure for the synthesis of polystyrene-grafted multiwalled carbon nanotubes using successive chemical modification steps to selectively introduce the polymer chains to the sidewalls and their self-assembly via anisotropic patchiness is presented.

Video: Grafting Multiwalled Carbon Nanotubes with Polystyrene to Enable Self-Assembly and Anisotropic Patchiness

Fabrication, Densification, and Replica Molding of 3D Carbon Nanotube Microstructures

The introduction of new materials and processes to microfabrication has, in large part, enabled many important advances in microsystems, lab-on-a-chip devices, and their applications. In particular, capabilities for cost-effective fabrication of polymer microstructures were transformed by the advent of soft lithography and other micromolding techniques 1, 2, and this led a revolution in applications of microfabrication to biomedical engineering and biology. Nevertheless, it remains challenging to fabricate microstructures with well-defined nanoscale surface textures, and to fabricate arbitrary 3D shapes at the micro-scale. Robustness of master molds and maintenance of shape integrity is especially important to achieve high fidelity replication of complex structures and preserving their nanoscale surface texture. The combination of hierarchical textures, and heterogeneous shapes, is a profound challenge to existing microfabrication methods that largely rely upon top-down etching using fixed mask templates. On the other hand, the bottom-up synthesis of nanostructures such as nanotubes and nanowires can offer new capabilities to microfabrication, in particular by taking advantage of the collective self-organization of nanostructures, and local control of their growth behavior with respect to microfabricated patterns. 
Our goal is to introduce vertically aligned carbon nanotubes (CNTs), which we refer to as CNT "forests", as a new microfabrication material. We present details of a suite of related methods recently developed by our group: fabrication of CNT forest microstructures by thermal CVD from lithographically patterned catalyst thin films; self-directed elastocapillary densification of CNT microstructures; and replica molding of polymer microstructures using CNT composite master molds. In particular, our work shows that self-directed capillary densification ("capillary forming"), which is performed by condensation of a solvent onto the substrate with CNT microstructures, significantly increases the packing density of CNTs. This process enables directed transformation of vertical CNT microstructures into straight, inclined, and twisted shapes, which have robust mechanical properties exceeding those of typical microfabrication polymers. This in turn enables formation of nanocomposite CNT master molds by capillary-driven infiltration of polymers. The replica structures exhibit the anisotropic nanoscale texture of the aligned CNTs, and can have walls with sub-micron thickness and aspect ratios exceeding 50:1. Integration of CNT microstructures in fabrication offers further opportunity to exploit the electrical and thermal properties of CNTs, and diverse capabilities for chemical and biochemical functionalization 3.

We present methods for fabrication of patterned microstructures of vertically aligned carbon nanotubes (CNTs), and their use as master molds for production of polymer microstructures with organized nanoscale surface texture. The CNT forests are densified by condensation of solvent onto the substrate, which significantly increases their packing density and enables self-directed formation of 3D shapes.

The introduction of new materials and processes to microfabrication has, in large part, enabled many important advances in microsystems, lab-on-a-chip ...

Engineering

Gyroid Nickel Nanostructures from Diblock Copolymer Supramolecules

Nanoporous metal foams possess a unique combination of properties - they are catalytically active, thermally and electrically conductive, and furthermore, have high porosity, high surface-to-volume and strength-to-weight ratio. Unfortunately, common approaches for preparation of metallic nanostructures render materials with highly disordered architecture, which might have an adverse effect on their mechanical properties. Block copolymers have the ability to self-assemble into ordered nanostructures and can be applied as templates for the preparation of well-ordered metal nanofoams. Here we describe the application of a block copolymer-based supramolecular complex - polystyrene-block-poly(4-vinylpyridine)(pentadecylphenol) PS-b-P4VP(PDP) - as a precursor for well-ordered nickel nanofoam. The supramolecular complexes exhibit a phase behavior similar to conventional block copolymers and can self-assemble into the bicontinuous gyroid morphology with two PS networks placed in a P4VP(PDP) matrix. PDP can be dissolved in ethanol leading to the formation of a porous structure that can be backfilled with metal. Using electroless plating technique, nickel can be inserted into the template&#39;s channels. Finally, the remaining polymer can be removed via pyrolysis from the polymer/inorganic nanohybrid resulting in nanoporous nickel foam with inverse gyroid morphology.

This article describes the preparation of well-ordered nickel nanofoams via electroless metal deposition onto nanoporous templates obtained from self-assembled diblock copolymer based supramolecules.

Nanoporous metal foams possess a unique combination of properties - they are catalytically active, thermally and electrically conductive, and furthermore, ...

Manufacturing of Three-dimensionally Microstructured Nanocomposites through Microfluidic Infiltration

Microstructured composite beams reinforced with complex three-dimensionally (3D) patterned nanocomposite microfilaments are fabricated via nanocomposite in&#64257;ltration of 3D interconnected microfluidic networks. The manufacturing of the reinforced beams begins with the fabrication of microfluidic networks, which involves layer-by-layer deposition of fugitive ink filaments using a dispensing robot, filling the empty space between filaments using a low viscosity resin, curing the resin and finally removing the ink.&#160;Self-supported 3D structures with other geometries and many layers (e.g.&#160;a few hundreds layers) could be built using this method. The resulting tubular micro&#64258;uidic networks are then infiltrated with thermosetting nanocomposite suspensions containing nanofillers (e.g.&#160;single-walled carbon nanotubes), and subsequently cured. The infiltration is done by applying a pressure gradient between two ends of the empty network (either by applying a vacuum or vacuum-assisted microinjection). Prior to the infiltration, the nanocomposite suspensions are prepared by dispersing nanofillers into polymer matrices using ultrasonication and three-roll mixing methods. The nanocomposites (i.e.&#160;materials infiltrated) are then solidified under UV exposure/heat cure, resulting in a 3D-reinforced composite structure. The technique presented here enables the design of functional nanocomposite macroscopic products for microengineering applications such as actuators and sensors.

Three-dimensional (3D) microstructured composite beams are fabricated through the directed and localized infiltration of nanocomposites into 3D porous microfluidic networks. The flexibility of this manufacturing method enables the utilization of different thermosetting materials and nanofillers in order to achieve a variety of functional 3D reinforced nanocomposite macroscopic products.

Microstructured composite beams reinforced with complex three-dimensionally (3D) patterned nanocomposite microfilaments are fabricated via nanocomposite ...

Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

We present a template-free method for &#8220;polymerizing&#8221; nanoparticles into long chains without side branches. A variety of nanoparticles are encapsulated in polystyrene-block-poly(acrylic acid) (PSPAA) shells and then used as monomers for their self-assembly. Spherical PSPAA micelles upon acid treatment are known to assemble into cylindrical micelles. Exploiting this tendency, the core-shell nanoparticles are induced to aggregate, coalesce, and then transform into long chains. When more than one type of nanoparticles are used, random and block &#8220;copolymers&#8221; of nanoparticles can be obtained. Detailed procedures are reported for the PSPAA encapsulation of nanoparticles, homo- and co-polymerization of the core-shell nanoparticles, separation and purification of the resulting nanoparticle chains. Transformations of single-line chains into double- and triple-line chains are also presented. The synergy between the polymer shell and the embedded nanoparticles leads to an unusual chain-growth polymerization mode, giving long nanoparticle chains that are distinct from the products of the traditional step-growth aggregation process.

Using Polystyrene-block-polyacrylic acid-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

We report protocols for &#8220;polymerizing&#8221; various types of polymer-encapsulated metal nanoparticles into long chains of &#8220;homo-&#8220; and &#8220;co-polymers&#8221;.

We present a template-free method for &#8220;polymerizing&#8221; nanoparticles into long chains without side branches. A variety of nanoparticles are ...

Functionalization of Single-walled Carbon Nanotubes with Thermo-reversible Block Copolymers and Characterization by Small-angle Neutron Scattering

We demonstrate a protocol for single-walled carbon nanotube functionalization using thermo-sensitive PEO-PPO-PEO triblock copolymers in an aqueous solution. In a carbon nanotube/PEO105-PPO70-PEO105 (poloxamer 407) aqueous solution, the amphiphilic poloxamer 407 adsorbs onto the carbon nanotube surfaces and self-assembles into continuous layers, driven by intermolecular interactions between constituent molecules. The addition of 5-methylsalicylic acid changes the self-assembled structure from spherical-micellar to a cylindrical morphology. The fabricated poloxamer 407/carbon nanotube hybrid particles exhibit thermo-responsive structural features so that the density and thickness of poloxamer 407 layers are also reversibly controllable by varying temperature. The detailed structural properties of the poloxamer 407/carbon nanotube particles in suspension can be characterized by small-angle neutron scattering experiments and model fit analyses. The distinct curve shapes of the scattering intensities depending on temperature control or addition of aromatic additives are well described by a modified core-shell cylinder model consisting of a carbon nanotube core cylinder, a hydrophobic shell, and a hydrated polymer layer. This method can provide a simple but efficient way for the fabrication and in-situ characterization of carbon nanotube-based nano particles with a structure-tunable encapsulation.

A method for the functionalization of carbon nanotubes with structure-tunable polymeric encapsulation layers and structural characterization using small-angle neutron scattering is presented.

We demonstrate a protocol for single-walled carbon nanotube functionalization using thermo-sensitive PEO-PPO-PEO triblock copolymers in an aqueous ...

Self-assembling Morphologies Obtained from Helical Polycarbodiimide Copolymers and Their Triazole Derivatives

A facile method for the preparation of polycarbodiimide-based secondary structures (e.g., nano-rings, &#34;craters,&#34; fibers, looped fibers, fibrous networks, ribbons, worm-like aggregates, toroidal structures, and spherical particles) is described. These aggregates are morphologically influenced by extensive hydrophobic side chain-side chain interactions of the singular polycarbodiimide strands, as inferred by atomic force microscopy (AFM) and scanning electron microscopy (SEM) techniques. Polycarbodiimide-g-polystyrene copolymers (PS-PCDs) were prepared by a combination of synthetic methods, including coordination-insertion polymerization, copper(I)-catalyzed azide alkyne cycloaddition (CuAAC) &#34;click&#34; chemistry, and atom transfer radical polymerization (ATRP). PS-PCDs were found to form specific toroidal architectures at low concentrations in CHCl3. To determine the influence of a more polar solvent medium (i.e., THF and THF/EtOH) on polymer aggregation behavior, a number of representative PS-PCD composites have been tested to show discrete concentration-dependent spherical particles. These fundamental studies are of practical interest to the development of experimental procedures for desirable architectures by directed self-assembly in thin film. These architectures may be exploited as drug carriers, whereas other morphological findings represent certain interest in the area of novel functional materials.

Here, we present a protocol to prepare and visualize secondary structures (e.g., fibers, toroidal architectures, and nano-spheres) derived from helical polycarbodiimides. The morphology characterized by both atomic force microscopy (AFM) and scanning electron microscopy (SEM) was shown to depend on molecular structure, concentration, and the solvent of choice.

A facile method for the preparation of polycarbodiimide-based secondary structures (e.g., nano-rings, &#34;craters,&#34; fibers, looped fibers, fibrous ...

Precision Milling of Carbon Nanotube Forests Using Low Pressure Scanning Electron Microscopy

A nanoscale fabrication technique appropriate for milling carbon nanotube (CNT) forests is described. The technique utilizes an environmental scanning electron microscope (ESEM) operating with a low pressure water vapor ambient. In this technique, a portion of the electron beam interacts with the water vapor in the vicinity of the CNT sample, dissociating the water molecules into hydroxyl radicals and other species by radiolysis. The remainder of the electron beam interacts with the CNT forest sample, making it susceptible to oxidation from the chemical products of radiolysis. This technique may be used to trim a selected region of an individual CNT, or it may be used to remove hundreds of cubic microns of material by adjusting ESEM parameters. The machining resolution is similar to the imaging resolution of the ESEM itself. The technique produces only small quantities of carbon residue along the boundaries of the cutting zone, with minimal effect on the native structural morphology of the CNT forest.

Low pressure scanning electron microscopy in a water vapor ambient is used to machine nanoscale to microscale features in carbon nanotube forests.

A nanoscale fabrication technique appropriate for milling carbon nanotube (CNT) forests is described. The technique utilizes an environmental scanning ...

Fabrication of a Bioactive, PCL-based "Self-fitting" Shape Memory Polymer Scaffold

Tissue engineering has been explored as an alternative strategy for the treatment of critical-sized cranio-maxillofacial (CMF) bone defects. Essential to the success of this approach is a scaffold that is able to conformally fit within an irregular defect while also having the requisite biodegradability, pore interconnectivity and bioactivity. By nature of their shape recovery and fixity properties, shape memory polymer (SMP) scaffolds could achieve defect &#8220;self-fitting.&#8221; In this way, following exposure to warm saline (~60 &#186;C), the SMP scaffold would become malleable, permitting it to be hand-pressed into an irregular defect. Subsequent cooling (~37 &#186;C) would return the scaffold to its relatively rigid state within the defect. To meet these requirements, this protocol describes the preparation of SMP scaffolds prepared via the photochemical cure of biodegradable polycaprolactone diacrylate (PCL-DA) using a solvent-casting particulate-leaching (SCPL) method. A fused salt template is utilized to achieve pore interconnectivity. To realize bioactivity, a polydopamine coating is applied to the surface of the scaffold pore walls. Characterization of self-fitting and shape memory behaviors, pore interconnectivity and in vitro bioactivity are also described.

Scaffolds capable of fitting within cranio-maxillofacial (CMF) bone defects while exhibiting osteoconductivity and bioactivity are of interest. This protocol describes the preparation of a shape memory scaffold based on polycaprolactone diacrylate (PCL-DA) using a solvent-casting particulate-leaching (SCPL) method employing a fused salt template and application of a bioactive polydopamine coating.

Tissue engineering has been explored as an alternative strategy for the treatment of critical-sized cranio-maxillofacial (CMF) bone defects. Essential to ...

Bioengineering

Multiscale Structures Aggregated by Imprinted Nanofibers for Functional Surfaces

Multiscale surface structures have attracted increasing interest owing to several potential applications in surface devices. However, an existing challenge in the field is the fabrication of hybrid micro-nano structures using a facile, cost-effective, and high-throughput method. To overcome these challenges, this paper proposes a protocol to fabricate multiscale structures using only an imprint process with an anodic aluminum oxide (AAO) filter and an evaporative self-aggregation process of nanofibers. Unlike previous attempts that have aimed to straighten nanofibers, we demonstrate a unique fabrication method for multiscale aggregated nanofibers with high aspect ratios. Furthermore, the surface morphology and wettability of these structures on various liquids were investigated to facilitate their use in multifunctional surfaces.

Presented is an easy method to fabricate nano-micro multiscale structures, for functional surfaces, by aggregating nanofibers fabricated using an anodic aluminum oxide filter.

Multiscale surface structures have attracted increasing interest owing to several potential applications in surface devices. However, an existing ...

Synthesis of Monodisperse Cylindrical Nanoparticles via Crystallization-driven Self-assembly of Biodegradable Block Copolymers

The production of monodisperse cylindrical micelles is a significant challenge in polymer chemistry. Most cylindrical constructs formed from diblock copolymers are produced by one of three techniques: thin film rehydration, solvent switching or polymerization-induced self-assembly, and produce only flexible, polydisperse cylinders. Crystallization-driven self-assembly (CDSA) is a method which can produce cylinders with these properties, by stabilizing structures of a lower curvature due to the formation of a crystalline core. However, the living polymerization techniques by which most core-forming blocks are formed are not trivial processes and the CDSA process may yield unsatisfactory results if carried out incorrectly. Here, the synthesis of cylindrical nanoparticles from simple reagents is shown. The drying and purification of reagents prior to a ring-opening polymerization of &#949;-caprolactone catalyzed by diphenyl phosphate is described. This polymer is then chain extended by methyl methacrylate (MMA) followed by N,N-dimethyl acrylamide (DMA) using reversible addition&#8722;fragmentation chain-transfer (RAFT) polymerization, affording a triblock copolymer that can undergo CDSA in ethanol. The living CDSA process is outlined, the results of which yield cylindrical nanoparticles up to 500 nm in length and a length dispersity as low as 1.05. It is anticipated that these protocols will allow others to produce cylindrical nanostructures and elevate the field of CDSA in the future.

Crystallization-driven self-assembly (CDSA) displays the unique ability to fabricate cylindrical nanostructures of narrow length distributions. The organocatalyzed ring-opening polymerization of &#949;-caprolactone and subsequent chain extensions of methyl methacrylate and N,N-dimethyl acrylamide are demonstrated. A living CDSA protocol that produces monodisperse cylinders up to 500 nm in length is outlined.

The production of monodisperse cylindrical micelles is a significant challenge in polymer chemistry. Most cylindrical constructs formed from diblock ...