Name: the preparation and properties of thermo-reversibly cross-linked rubber via diels-alder chemistry
Uploaded: 2016-08-25T15:00:00.000+00:00
Duration: 7 min 2 s
Description: Watch this Scientific Journal Video about The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry at JoVE.com

This research forms part of the research program of the Dutch Polymer Institute, project #749.

1. Rubber Modification
<ol>
	<li>Prepare the maleated EPM (EPM-g-MA, 49 wt% ethylene, 2.1 wt% MA, Mn = 50 kg/mol, PDI = 2.0) rubber and furfurylamine (FFA) before starting the experiment as indicated in steps 1.1.1-1.1.4.5
	<ol>
		<li>Dry the EPM-g-MA rubber in a vacuum oven for one hour at 175 &#176;C to convert present di-acid into anhydride.11</li>
		<li>Compression mold a 0.1 mm thick rubber film in a hot press for 10 min at 150 &#176;C and 100 bar.</li>
		<li>Record a transmission infrared spectrum of the resulting film after placing it in a KBr tablet holder. 
		NOTE: The conversion of the hydrolyzed di-acid into anhydride is complete if the typical carboxylic acid peak (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-sCO.jpg" /> = 1,710 cm-1) is absent and the characteristic cyclic anhydride peak (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-asCO.jpg" /> = 1,856 cm-1) is present.5</li>
		<li>Using standard distillation glassware, distill 2.8 g FFA (boiling point = 145 &#176;C, 28.9 mmol; 3.0 eq. based on MA content in EPM-g-MA) under atmospheric pressure.</li>
	</ol>
	</li>
	<li>Prepare a 10 wt% rubber solution by weighing 45.0 g of EPM-g-MA rubber (9.6 mmol MA) and dissolving it in 500 ml tetrahydrofuran (THF) at 23 &#176;C in a closed beaker under vigorous stirring.</li>
	<li>Add the 2.8 g freshly distilled FFA to the 10 wt% rubber solution.</li>
	<li>Stir the reaction mixture in a closed system at 23 &#176;C for at least 1 hr.</li>
	<li>Precipitate the reaction mixture by pouring it slowly into a tenfold (5 L) of acetone under mechanical stirring, yielding the polymer product as white threads that are easily fished out of the beaker using large tweezers.</li>
	<li>Dry the collected product (EPM-g-furan) to constant weight in a vacuum oven at 35 &#176;C (this takes approximately 1 day).</li>
	<li>Compression mold the resulting, slightly yellowish product in a mold between two metal plates in a hot press for 10 min at 175 &#176;C and 100 bar to convert the intermediate maleamic acid product into the imide product.</li>
	<li>Cut the resulting plaque of rubber in small pieces (0.05 g) with scissors and wash them thoroughly by immersing them in acetone to remove any unreacted FFA.</li>
	<li>Record a transmission infrared spectrum of the product in a KBr tablet holder after compression molding it into a 0.1 mm thick film.5 
	NOTE: The absence of any remaining amide-acid can be deduced from the absence of a peak at 1,530 cm-1.39, 40 The most illustrative indication for the successful modification are the nearly complete disappearance of <img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-asCO.jpg" /> at 1,856 cm-1 of the anhydride and the appearance of <img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-sCO.jpg" /> at 1,710 cm-1 and the C-N stretching vibration (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-sCN.jpg" /> = 1,378 cm-1) of the maleimide.</li>
	<li>Determine the reaction conversion of EPM-g-MA to EPM-g-furan from the decrease in absorbance of the C=O symmetrical stretch vibration of the anhydride groups (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-asCO.jpg" />= 1,856 cm-1) by integrating the areas under the individual infrared (FT-IR) peaks after deconvolution (R2 &#62; 0.95).5 
	NOTE: The methyl rocking vibration (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_rho_ip_CH3.jpg" /> = 723 cm-1), originating from the EPM backbone, remains unchanged upon modification and can be used as an internal reference.</li>
	<li>Determine the modification conversions by performing Elemental Analysis (EA) for N, C and H on the washed and dried rubber samples.5 
	NOTE: The molar contents can be derived from the measured mass percentages. The molar nitrogen content in EPM-g-furan is equal to that of the grafted furan groups. The conversion can be calculated by comparing the molar ratio of MA-grafted monomer to the non-grafted EPM monomers in the EPM-g-MA precursor (7.69 x 10-3) with the molar ratio N:EPM of the EPM-g-furan sample.</li>
	<li>Measure the Shore A Hardness of the compression molded samples at least 10 times pressing a durometer onto a rubber sample, covering the entire cylindrical surface of the Durometer.5 
	NOTE: Samples with a thickness of 2 &#177; 0.1 mm should be used for these tests.</li>
	<li>Measure the elongation (at break) and the ultimate tensile strength by performing tensile tests on samples of approximately 1 mm thick and 5 mm wide using a clamp length of 15 mm and a strain rate of 500 &#177; 50 mm/min. Determine the Young&#39;s modulus from the initial slope of the resulting stress-strain curves. 
	NOTE: For each measurement, test 10 samples and exclude two outliers with the highest and the lowest values.</li>
	<li>Determine the compression set at 23 &#176;C by compressing cylindrical samples with a thickness of 6 &#177; 0.1 mm (t0) and a diameter of 13 &#177; 0.1 mm between to metal plates to 3/4th of their initial thickness (tn) for 70 hr, let them relax at 50 &#176;C for &#189; hr and measure the thickness (ti). 
	NOTE: The compression set value can be determined from (t0-ti)/(t0-tn).</li>
</ol>
2. Diels-Alder Cross-linking and Reprocessing
<ol>
	<li>Before the experiment, synthesize the aliphatic bismaleimide (BM) from didodecylamine and maleic anhydride (MA) according to a reported procedure.41</li>
	<li>Weigh 40.0 g of EPM-g-furan rubber (8.6 mmol furan content) and 0.04 g phenolic anti-oxidant (octadecyl-1-[3,5-di-tert-butyl-4-hydroxyphenyl]propionate) and dissolve them in a large, closed beaker with 500 ml THF at 23 &#176;C.</li>
	<li>Add 1.48 g of the aliphatic bismaleimide (4.3 mmol, 0.5 eq. based on furan content in EPM-g-furan) to beaker with the 10 wt% solution.</li>
	<li>Stir the reaction mixture for at least 1 hr at 50 &#176;C in the closed beaker, then remove the cap to open the system to evaporate the solvent. Evaporation of the THF can also be performed using a rotary evaporator.</li>
	<li>Dry the collected product to constant weight in a vacuum oven at 35 &#176;C.</li>
	<li>Compression mold the product for 30 min at 175 &#176;C and 100 bar.</li>
	<li>Anneal the resulting product by storing it in an oven at 50 &#176;C for at least three days.</li>
	<li>Cut the resulting plaque of rubber in small pieces (0.05 g) using scissors and wash them thoroughly by immersing them in acetone to remove any unreacted components and compression mold it into a 0.1 mm thick film.</li>
	<li>Record an transmission infrared spectrum of the resulting film in a KBr tablet holder, using the same set-up as described for 1.9.1.5</li>
	<li>Determine the cross-linking conversion from relative decrease in the C-O-C symmetric stretch vibration of the furan rings (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-sCOC.jpg" /> = 1,013 cm-1) as described in 1.10.5</li>
	<li>Determine the cross-linking conversion by performing EA for N, C and H on the washed and dried rubber samples.5</li>
	<li>Determine the Shore A hardness, Young&#39;s modulus, the elongation at break, the ultimate tensile strength and compression set at 23 &#176;C in the same way as described in 1.12-14.</li>
	<li>Reprocess the samples after testing by cutting them into small pieces using scissors (&#177; 50 mm3) and compression molding these under the same conditions into new, homogeneous samples with the same dimensions.</li>
</ol>
3. Peroxide and Sulfur Curing of ENB-EPDM
<ol>
	<li>Heat an internal batch mixer to 70 &#176;C and let it rotate at 50 rpm. 
	NOTE: An initial conditioning step by flushing the chamber with nitrogen gives better control of the cross-linking processes.</li>
	<li>Feed 18.1 g of ENB-EPDM (48 wt% ethylene, 5.5 wt% ENB) to the internal batch mixer to reach a 70% fill factor and mix for 2 min to yield a homogeneous melt.</li>
	<li>Feed 1.25 phr of peroxide di(tert-butylperoxy-isopropyl) benzene) or 1.88 phr of a 80% pure, standard, semi-efficient sulfur vulcanization system and mix it with the rubber for 3 min at 70 &#176;C.</li>
	<li>Compression mold the resulting compound in a hot press for 30 min at 175 &#176;C and 100 bar to cure it.</li>
	<li>Determine the Shore A hardness, Young&#39;s modulus, the elongation at break and the ultimate tensile strength compression set in the same way as described in 1.12-14.</li>
</ol>
4. Cross-link Density Determination
<ol>
	<li>Cut a piece of compression molded, cross-linked rubber of approximately 50 mg using scissors.
	<ol>
		<li>Determine the initial weight of the rubber sample precisely by weighing it in a 20 ml glass vial (W0).</li>
		<li>Immerse the weighed rubber in 15 ml of decalin.</li>
	</ol>
	</li>
	<li>Let the rubber swell in the decalin until its weight does not increase anymore and equilibrium swelling is reached (approximately 3 days).</li>
	<li>Carefully take the swollen sample out of the vial and carefully dab the surface with a paper tissue to remove any solvent from the surface without squeezing it.</li>
	<li>Weigh the swollen rubber sample in a new sample vial (W1).</li>
	<li>Dry the swollen sample in a vacuum oven at 80 &#176;C until a constant weight is reached and determine the sample&#39;s dry weight (W2).</li>
	<li>Obtain the gel content from W2/W0 x 100%</li>
	<li>Determine the cross-link density ([XLD] in mol/cm3) using the Flory-Rehner equation 42, 43, [XLD]= (ln(1-VR)+VR +&#967;VR2)/(2VS(0.5VR-VR1/3) ) with VS the molar volume of the solvent (decalin: 154 ml/mol at 23 &#176;C), &#967; the interaction parameter (decalin-EPDM: 0.121 + 0.278VR44) and VR the volume fraction of rubber in swollen sample that can be determined from W2/(W2+(W1-W2)&#8729;&#961;EPM-g-furan/&#961;decalin) with the densities (&#961;) being 860 kg/m3 for EPM-g-furan and 896 kg/m3 for decalin, respectively.</li>
</ol>

The author Martin van Duin is an employee of LANXESS Elastomers B.V. that produces EPM-g-MA rubbers used in this Article.

A commercial EPM-g-MA rubber was thermo-reversibly cross-linked in a simple two-step approach. The maleated rubber was first modified with FFA to graft furan groups onto the rubber backbone. The resulting pending furans show reactivity as Diels-Alder dienes. An aliphatic BM was used as cross-linking agent, resulting in a thermo-reversible bridge between two furan moieties. Both reactions were successful with good conversions (&#62; 80%) according to infrared spectroscopy, elemental analysis. Cross-linking was shown by sw...

Sulfur vulcanization and peroxide curing are currently the main industrial cross-linking techniques in the rubber industry, yielding irreversible chemical cross-links that prevent melt reprocessing.1, 2 A &#39;cradle to cradle&#39; approach to recycle cross-linked rubbers requires a material that behaves similar to permanently cross-linked rubbers at service conditions, while having the processability and complete recyclability of a thermoplastic at high temperatures. An approach to achieve such recyclability uses rubbery networks with reversible cross-links that respond to an external stimulus, such as temperature (most feasible from the viewpoint of future industrial applications).3-5 The formation of these cross-links at relatively low service temperatures is required for good mechanical behavior of the rubber, while their cleavage at high temperatures (similar to processing temperature of original non-cross-linked compound) allows for recycling of the material.
Some specific materials can be reversibly cross-linked by making use of so-called dynamic covalent networks via polycondensation reactions6 or by so-called reversible network topology freezing via transesterification reactions.7-9 The disadvantage of these approaches is the necessity of designing and synthesizing new polymers rather than modifying existing, commercial rubbers that already have the desired properties. Techniques to thermo-reversibly cross-link rubbers involve hydrogen bonding, ionic interactions and covalent bonding such as via thermo-activated disulfide rearrangements.10-13 Recently, thermo-reversible cross-linking via Diels-Alder (DA) chemistry was developed.14-21 DA chemistry can be applied to a broad range of polymers and represents a popular choice, especially since the DA reaction allows for relatively fast kinetics and mild reaction conditions.17, 22-24 Their low coupling and high decoupling temperatures make furan and maleimide excellent candidates for reversible polymer cross-linking.18-20, 25-28
The aim of the present work is to provide a method for the use of DA chemistry as a thermo-reversible cross-linking tool for an industrial rubber product (Figure 1).5 First, the reactivity of saturated hydrocarbon elastomers, such as ethylene/propylene rubbers (EPM), has to be increased. A commercially relevant example that facilitates this is the peroxide-initiated free-radical grafting of maleic anhydride (MA).29-34 Secondly, a furan group can be grafted onto such a maleated EPM rubber by inserting furfurylamine (FFA) into the pendant anhydride to form an imide.35, 36 Finally, the furan moieties that are thus attached to the rubber backbone can then participate in thermo-reversible DA chemistry as an electron-rich diene.25, 37 The electron-poor bis-maleimide (BM) is a suitable dienophile for this cross-linking reaction.19, 26, 38
<img alt="Figure 1" src="/files/ftp_upload/54496/54496fig1.jpg" /> 
Figure 1. Reaction scheme. Furan grafting and bismaleimide cross-linking of EPM-g-MA rubber (reprinted with permission from 5). <a href="https://www-jove-com.bdigitaluss.remotexs.co/files/ftp_upload/54496/54496fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

<table><tbody><tr><td>ENB-EPDM</td><td>LANXESS Elastomers B.V.</td><td>Keltan 8550C</td><td></td></tr><tr><td>EPM-g-MA</td><td>LANXESS Elastomers B.V.</td><td>Keltan DE5005</td><td>Vacuum oven for one hour at 175&amp;nbsp;&amp;deg;C</td></tr><tr><td>furfurylamine</td><td>Sigma-Aldrich</td><td>F20009</td><td>Freshly distillated before use</td></tr><tr><td>di-dodecylamine</td><td>Sigma-Aldrich</td><td>36784</td><td></td></tr><tr><td>maleic anhydride</td><td>Sigma-Aldrich</td><td>M0357</td><td></td></tr><tr><td>octadecyl-1-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate</td><td>Sigma-Aldrich</td><td>367079</td><td></td></tr><tr><td>bis(tert-butylperoxy-iso-propyl) benzene</td><td>Sigma-Aldrich</td><td>531685</td><td></td></tr><tr><td>tetrahydrofuran</td><td>Sigma-Aldrich</td><td>401757</td><td></td></tr><tr><td>decalin</td><td>Sigma-Aldrich</td><td>294772</td><td></td></tr><tr><td>acetone</td><td>Sigma-Aldrich</td><td>320110</td><td></td></tr></tbody></table>

the preparation and properties of thermo-reversibly cross-linked rubber via diels-alder chemistry

A method for using Diels Alder thermo-reversible chemistry as cross-linking tool for rubber products is demonstrated. In this work, a commercial ethylene-propylene rubber, grafted with maleic anhydride, is thermo-reversibly cross-linked in two steps. The pending anhydride moieties are first modified with furfurylamine to graft furan groups to the rubber backbone. These pendant furan groups are then cross-linked with a bis-maleimide via a Diels-Alder coupling reaction. Both reactions can be performed under a broad range of experimental conditions and can easily be applied on a large scale. The material properties of the resulting Diels-Alder cross-linked rubbers are similar to a peroxide-cured ethylene/propylene/diene rubber (EPDM) reference. The cross-links break at elevated temperatures (&#62; 150 &#176;C) via the retro-Diels-Alder reaction and can be reformed by thermal annealing at lower temperatures (50-70 &#176;C). Reversibility of the system was proven with infrared spectroscopy, solubility tests and mechanical properties. Recyclability of the material was also shown in a practical way, i.e., by cutting a cross-linked sample into small parts and compression molding them into new samples displaying comparable mechanical properties, which is not possible for conventionally cross-linked rubbers.

The successful modification of EPM-g-MA into EPM-g-furan and the cross-linking with the bismaleimide is shown by Fourier transform infrared spectrometry (FTIR) (Figure 2). The presence of furan groups in the EPM-g-furan product can be deduced from the splitting of the CC aliphatic stretching peak (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-sCC.jpg" /> = 1,050 cm-1) into two furan peaks (<img alt="Equation" src="/files/ftp_upload/54496/54496eq_v-...

Watch this Scientific Journal Video about The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry at JoVE.com

The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry

A simple two-step approach involving rubber modification and cross-linking yields fully reworkable, elastic rubber products.

A method for using Diels Alder thermo-reversible chemistry as cross-linking tool for rubber products is demonstrated. In this work, a commercial ...

the-preparation-properties-thermo-reversibly-cross-linked-rubber-via

Research

Education

JoVE Core

JoVE Journal

Organic Chemistry

Chemistry

Unit 1

Dienes, Conjugated Pi Systems, and Pericyclic Reactions

SCIENTISTS IN ACTION

13.6K Views.  University of Groningen. A simple two-step approach involving rubber modification and cross-linking yields fully reworkable, elastic rubber products. 

Video: The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry

A Facile and Efficient Approach for the Production of Reversible Disulfide Cross-linked Micelles

Nanomedicine is an emerging form of therapy that harnesses the unique properties of particles that are nanometers in scale for biomedical application. Improving drug delivery to maximize therapeutic outcomes and to reduce drug-associated side effects are some of the cornerstones of present-day nanomedicine. Nanoparticles in particular have found a wide application in cancer treatment. Nanoparticles that offer a high degree of flexibility in design, application, and production based on the tumor microenvironment are projected to be more effective with rapid translation into clinical practice. The polymeric micellar nano-carrier is a popular choice for drug delivery applications.
In this article, we describe a simple and effective protocol for synthesizing drug-loaded, disulfide cross-linked micelles based on the self-assembly of a well-defined amphiphilic linear-dendritic copolymer (telodendrimer, TD). TD is composed of polyethylene glycol (PEG) as the hydrophilic segment and a thiolated cholic acid cluster as the core-forming hydrophobic moiety attached stepwise to an amine-terminated PEG using solution-based peptide chemistry. Chemotherapy drugs, such as paclitaxel (PTX), can be loaded using a standard solvent evaporation method. The O2-mediated oxidation was previously utilized to form intra-micellar disulfide cross-links from free thiol groups on the TDs. However, the reaction was slow and not feasible for large-scale production. Recently, an H2O2-mediated oxidation method was explored as a more feasible and efficient approach, and it was 96 times faster than the previously reported method. Using this approach, 50 g of PTX-loaded, disulfide cross-linked nanoparticles have been successfully produced with narrow particle size distribution and high drug loading efficiency. The stability of the resulting micelle solution is analyzed using disrupting conditions such as co-incubation with a detergent, sodium dodecyl sulfate, with or without a reducing agent. The drug-loaded, disulfide cross-linked micelles demonstrated less hemolytic activity when compared to their non-cross-linked counterparts.

To deliver cancer drugs to tumor sites with high specificity and reduced side effects, new methods based on nanoparticles are required. Here, we describe disulfide cross-linked micelles that can be easily prepared by hydrogen peroxide-mediated oxidation and are able to dissociate efficiently under a reducing tumor environment to release payloads.

Nanomedicine is an emerging form of therapy that harnesses the unique properties of particles that are nanometers in scale for biomedical application. ...

Biochemistry

Synthesis of Programmable Main-chain Liquid-crystalline Elastomers Using a Two-stage Thiol-acrylate Reaction

This study presents a novel two-stage thiol-acrylate Michael addition-photopolymerization (TAMAP) reaction to prepare main-chain liquid-crystalline elastomers (LCEs) with facile control over network structure and programming of an aligned monodomain. Tailored LCE networks were synthesized using routine mixing of commercially available starting materials and pouring monomer solutions into molds to cure. An initial polydomain LCE network is formed via a self-limiting thiol-acrylate Michael-addition reaction. Strain-to-failure and glass transition behavior were investigated as a function of crosslinking monomer, pentaerythritol tetrakis(3-mercaptopropionate) (PETMP). An example non-stoichiometric system of 15 mol% PETMP thiol groups and an excess of 15 mol% acrylate groups was used to demonstrate the robust nature of the material. The LCE formed an aligned and transparent monodomain when stretched, with a maximum failure strain over 600%. Stretched LCE samples were able to demonstrate both stress-driven thermal actuation when held under a constant bias stress or the shape-memory effect when stretched and unloaded. A permanently programmed monodomain was achieved via a second-stage photopolymerization reaction of the excess acrylate groups when the sample was in the stretched state. LCE samples were photo-cured and programmed at 100%, 200%, 300%, and 400% strain, with all samples demonstrating over 90% shape fixity when unloaded. The magnitude of total stress-free actuation increased from 35% to 115% with increased programming strain. Overall, the two-stage TAMAP methodology is presented as a powerful tool to prepare main-chain LCE systems and explore structure-property-performance relationships in these fascinating stimuli-sensitive materials.

A novel methodology is presented to synthesize and program main-chain liquid-crystalline elastomers using commercially available starting monomers. A wide range of thermomechanical properties was tailored by adjusting the amount of crosslinker, while the actuation performance was dependent on the amount of applied strain during programming.

This study presents a novel two-stage thiol-acrylate Michael addition-photopolymerization (TAMAP) reaction to prepare main-chain liquid-crystalline ...

Facile Synthesis of Worm-like Micelles by Visible Light Mediated Dispersion Polymerization Using Photoredox Catalyst

Presented herein is a protocol for the facile synthesis of worm-like micelles by visible light mediated dispersion polymerization. This approach begins with the synthesis of a hydrophilic poly(oligo(ethylene glycol) methyl ether methacrylate) (POEGMA) homopolymer using reversible addition-fragmentation chain-transfer (RAFT) polymerization. Under mild visible light irradiation (&#955; = 460 nm, 0.7 mW/cm2), this macro-chain transfer agent (macro-CTA) in the presence of a ruthenium based photoredox catalyst, Ru(bpy)3Cl2 can be chain extended with a second monomer to form a well-defined block copolymer in a process known as Photoinduced Electron Transfer RAFT (PET-RAFT). When PET-RAFT is used to chain extend POEGMA with benzyl methacrylate (BzMA) in ethanol (EtOH), polymeric nanoparticles with different morphologies are formed in situ according to a polymerization-induced self-assembly (PISA) mechanism. Self-assembly into nanoparticles presenting POEGMA chains at the corona and poly(benzyl methacrylate) (PBzMA) chains in the core occurs in situ due to the growing insolubility of the PBzMA block in ethanol. Interestingly, the formation of highly pure worm-like micelles can be readily monitored by observing the onset of a highly viscous gel in situ due to nanoparticle entanglements occurring during the polymerization. This process thereby allows for a more reproducible synthesis of worm-like micelles simply by monitoring the solution viscosity during the course of the polymerization. In addition, the light stimulus can be intermittently applied in an ON/OFF manner demonstrating temporal control over the nanoparticle morphology.

This article describes a process for producing polymeric self-assembled nanoparticles using visible light mediated dispersion polymerization. Using low energy visible light to control the polymerization allows for the reproducible formation of self-assembled worm-like micelles at high solids content.

Presented herein is a protocol for the facile synthesis of worm-like micelles by visible light mediated dispersion polymerization. This approach begins ...

Synthesis of Soft Polysiloxane-urea Elastomers for Intraocular Lens Application

This study discusses a synthesis route for soft polysiloxane-based urea (PSU) elastomers for their applications as accommodating intraocular lenses (a-IOLs). Aminopropyl-terminated polydimethylsiloxanes (PDMS) were previously prepared via the ring-chain equilibration of the cyclic siloxane octamethylcyclotetrasiloxane (D4) and 1,3-bis(3-aminopropyl)-tetramethyldisiloxane (APTMDS). Phenyl groups were introduced into the siloxane backbone via the copolymerization of D4 and 2,4,6,8-tetramethyl-2,4,6,8-tetraphenyl-cyclotetrasiloxane (D4Me,Ph). These polydimethyl-methyl-phenyl-siloxane-block copolymers were synthesized for increasing the refractive indices of polysiloxanes. For applications as an a-IOL, the refractive index of the polysiloxanes must be equivalent to that of a young human eye lens. The polysiloxane molecular weight is controlled by the ratio of the cyclic siloxane to the endblocker APTMDS. The transparency of the PSU elastomers is examined by the transmittance measurement of films between 200 and 750 nm, using a UV-Vis spectrophotometer. Transmittance values at 750 nm (upper end of the visible spectrum) are plotted against the PDMS molecular weight, and &#62; 90% of the transmittance is observed until a molecular weight of 18,000 g&#183;mol&#8722;1. Mechanical properties of the PSU elastomers are investigated using stress-strain tests on die-cut dog-bone-shaped specimens. For evaluating mechanical stability, mechanical hysteresis is measured by repeatedly stretching (10x) the specimens to 5% and 100% elongation. Hysteresis considerably decreases with the increase in the PDMS molecular weight. In vitro cytotoxicity of some selected PSU elastomers is evaluated using an MTS cell viability assay. The methods described herein permit the synthesis of a soft, transparent, and noncytotoxic PSU elastomer with a refractive index approximately equal to that of a young human eye lens.

This study describes synthetic routes for aminopropyl-terminated polydimethylsiloxanes and polydimethyl-methyl-phenyl-siloxane-block copolymers and for soft polysiloxane-based urea (PSU) elastomers. It presents the application of PSUs as accommodating an intraocular lens. An evaluation method for in vitro cytotoxicity is also described.

This study discusses a synthesis route for soft polysiloxane-based urea (PSU) elastomers for their applications as accommodating intraocular lenses ...

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in Poly(S-Divinylbenzene)

Elemental sulfur (S8) is a byproduct of the petroleum industry with millions of tons produced annually. Such abundant production and limited applications lead to sulfur as a cost-efficient reagent for polymer synthesis. Inverse vulcanization combines elemental sulfur with a variety of monomers to form functional polysulfides without the need for solvents. Short reaction times and straight forward synthetic methods have led to rapid expansion of inverse vulcanization. However, high reaction temperatures (&#62;160 &#176;C) limit the types of monomers that can be used. Here, the dynamic sulfur bonds in poly(S-divinylbenzene) are used to initiate polymerization at much lower temperatures. The S-S bonds in the prepolymer are less stable than S-S bonds in S8, allowing radical formation at 90 &#176;C rather than 159 &#176;C. A variety of allyl and vinyl ethers have been incorporated to form terpolymers. The resulting materials were characterized by 1H NMR, gel permeation chromatography, and differential scanning calorimetry, as well as examining changes in solubility. This method expands on the solvent-free, thiyl radical chemistry utilized by inverse vulcanization to create polysulfides at mild temperatures. This development broadens the range of monomers that can be incorporated thus expanding the accessible material properties and possible applications.

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene

The goal of this protocol is to initiate polymerization using dynamic sulfur bonds in poly(S-divinylbenzene) at mild temperatures (90 &#176;C) without using solvents. Terpolymers are characterized by GPC, DSC and 1H NMR, and tested for changes in solubility.

Elemental sulfur (S8) is a byproduct of the petroleum industry with millions of tons produced annually. Such abundant production and limited applications ...

Three-dimensional Biomimetic Technology: Novel Biorubber Creates Defined Micro- and Macro-scale Architectures in Collagen Hydrogels

Tissue scaffolds play a crucial role in the tissue regeneration process. The ideal scaffold must fulfill several requirements such as having proper composition, targeted modulus, and well-defined architectural features. Biomaterials that recapitulate the intrinsic architecture of in vivo tissue are vital for studying diseases as well as to facilitate the regeneration of lost and malformed soft tissue. A novel biofabrication technique was developed which combines state of the art imaging, three-dimensional (3D) printing, and selective enzymatic activity to create a new generation of biomaterials for research and clinical application. The developed material, Bovine Serum Albumin rubber, is reaction injected into a mold that upholds specific geometrical features. This sacrificial material allows the adequate transfer of architectural features to a natural scaffold material. The prototype consists of a 3D collagen scaffold with 4 and 3 mm channels that represent a branched architecture. This paper emphasizes the use of this biofabrication technique for the generation of natural constructs. This protocol utilizes a computer-aided software (CAD) to manufacture a solid mold which will be reaction injected with BSA rubber followed by the enzymatic digestion of the rubber, leaving its architectural features within the scaffold material.

An innovative biofabrication technique was developed to engineer three-dimensional constructs that resemble the architectural features, components, and mechanical properties of in vivo tissue. This technique features a newly developed sacrificial material, BSA rubber, which transfers detailed spatial features, reproducing the in vivo architectures of a wide variety of tissues.

Tissue scaffolds play a crucial role in the tissue regeneration process. The ideal scaffold must fulfill several requirements such as having proper ...

Bioengineering

Evaluation of the Curing of Adhesive Systems by Rheological and Thermal Testing

The analysis of thermal processes associated to the curing of adhesives and the study of mechanical behavior once cured, provide key information to choose the best option for any specific application. The proposed methodology for the curing characterization, based on thermal analysis and rheology, is described through the comparison of three commercial adhesives. The experimental techniques used here are Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC) and Rheology. TGA provides information about the thermal stability and filler content, DSC allows the evaluation of some thermal events associated to the cure reaction and to thermal changes of the cured material when subjected to temperature changes. Rheology complements the information of the thermal transformations from a mechanical point of view. Thus, the curing reaction can be tracked through the elastic modulus (mainly the storage modulus), the phase angle and the gap. In addition, it is also shown that although DSC is of no use to study the curing of moisture curable adhesives, it is a very convenient method to evaluate the low temperature glass transition of amorphous systems.

An experimental methodology based on thermal and rheological measurements is proposed to characterize the curing process of adhesives with to obtain useful information for industrial adhesive selection.

The analysis of thermal processes associated to the curing of adhesives and the study of mechanical behavior once cured, provide key information to choose ...

Engineering

Fabricating Degradable Thermoresponsive Hydrogels on Multiple Length Scales via Reactive Extrusion, Microfluidics, Self-assembly, and Electrospinning

While various smart materials have been explored for a variety of biomedical applications (e.g., drug delivery, tissue engineering, bioimaging, etc.), their ultimate clinical use has been hampered by the lack of biologically-relevant degradation observed for most smart materials. This is particularly true for temperature-responsive hydrogels, which are almost uniformly based on polymers that are functionally non-degradable (e.g., poly(N-isopropylacrylamide) (PNIPAM) or poly(oligoethylene glycol methacrylate) (POEGMA)). As such, to effectively translate the potential of thermoresponsive hydrogels to the challenges of remote-controlled or metabolism-regulated drug delivery, cell scaffolds with tunable cell-material interactions, theranostic materials with the potential for both imaging and drug delivery, and other such applications, a method is required to render the hydrogels (if not fully degradable) at least capable of renal clearance following the required lifetime of the material. To that end, this protocol describes the preparation of hydrolytically-degradable hydrazone-crosslinked hydrogels on multiple length scales based on the reaction between hydrazide and aldehyde-functionalized PNIPAM or POEGMA oligomers with molecular weights below the renal filtration limit. Specifically, methods to fabricate degradable thermoresponsive bulk hydrogels (using a double barrel syringe technique), hydrogel particles (on both the microscale through the use of a microfluidics platform facilitating simultaneous mixing and emulsification of the precursor polymers and the nanoscale through the use of a thermally-driven self-assembly and cross-linking method), and hydrogel nanofibers (using a reactive electrospinning strategy) are described. In each case, hydrogels with temperature-responsive properties similar to those achieved via conventional free radical cross-linking processes can be achieved, but the hydrazone cross-linked network can be degraded over time to re-form the oligomeric precursor polymers and enable clearance. As such, we anticipate these methods (which may be generically applied to any synthetic water-soluble polymer, not just smart materials) will enable easier translation of synthetic smart materials to clinical applications.

Protocols are described for the fabrication of degradable thermoresponsive hydrogels based on hydrazone cross-linking of polymeric oligomers on the bulk scale, microscale, and nanoscale, the latter for preparation of both gel nanoparticles and nanofibers.

While various smart materials have been explored for a variety of biomedical applications (e.g., drug delivery, tissue engineering, bioimaging, etc.), ...

Designed for Molecular Recycling: A Lignin-Derived Semi-aromatic Biobased Polymer

The development of chemically recyclable biopolymers offers opportunities within the pursuit of a circular economy. Chemically recyclable biopolymers make a positive effort to solve the issue of polymer materials in the disposal phase after the use phase. In this paper, the production of biobased semi-aromatic polyesters, which can be extracted entirely from biomass such as lignin, is described and visualized. The polymer poly-S described in this paper has thermal properties similar to certain commonly used plastics, such as PET. We developed a Green Knoevenagel reaction, which can efficiently produce monomers from aromatic aldehydes and malonic acid. This reaction has been proven to be scalable and has a remarkably low calculated E-factor. These polyesters with ligno-phytochemicals as a starting point show an efficient molecular recycling with minimal losses. The polyester poly(dihydrosinapinic acid) (poly-S) is presented as an example of these semi-aromatic polyesters, and the polymerization, depolymerization, and re-polymerization are described.

An example of a closed-loop approach towards a circular materials economy is described here. A whole sustainable cycle is presented where biobased semi-aromatic polyesters are designed by polymerization, depolymerization, and then re-polymerized with only slight changes in their yields or final properties.

The development of chemically recyclable biopolymers offers opportunities within the pursuit of a circular economy. Chemically recyclable biopolymers make ...

Depolymerizable Olefinic Polymers Based on Fused-Ring Cyclooctene Monomers

The growing consumption of synthetic polymers and the accumulation of polymer waste have led to a pressing need for new routes to sustainable materials. Achieving a closed-loop polymer economy via chemical recycling to monomer (CRM) is one such promising route. Our group recently reported a new CRM system based on polymers prepared by ring-opening metathesis polymerization (ROMP) of trans-cyclobutane fused cyclooctene (tCBCO) monomers. This system offers several key advantages, including the ease of polymerization at ambient temperatures, quantitative depolymerization to monomers under mild conditions, and a broad range of functionalities and thermomechanical properties. Here, we outline detailed protocols for the preparation of tCBCO-based monomers and their corresponding polymers, including the preparation of elastic polymer networks and compression molding of linear thermoplastic polymers. We also outline the preparation of high ring strain E-alkene tCBCO monomers and their living polymerization. Finally, the procedures for the depolymerization of linear polymers and polymer networks are also demonstrated.

Here, we describe protocols for the preparation of trans-cyclobutane fused cyclooctenes (tCBCO),&#160;their polymerization to prepare depolymerizable olefinic polymers, and the depolymerization of these polymers under mild conditions. Additionally, protocols for the preparation of depolymerizable networks and compression molding of rigid linear plastics based on this system are described.

The growing consumption of synthetic polymers and the accumulation of polymer waste have led to a pressing need for new routes to sustainable materials. ...